用氟硅酸锌制备折射率可变的过渡层，本项发明专利技术所属域为新型光电子材料。为了解决ＳｎＯ↓［２］：Ｆ沉积薄膜的衍射光斑，需要在玻璃与ＳｎＯ↓［２］：Ｆ层之间加入一层透明过渡层薄膜。本发明专利技术主要是采用氟硅酸锌，用热喷涂的方法，在加热的玻璃表面，沉积出ＳｉＯ↓［２］膜和ＳｉＯ↓［２］与其他金属氧化物构成的多组分薄膜。通过改变添加金属盐在反应前驱液中所占百分比，可以方便的调整沉积薄膜的折射率。本发明专利技术沉积的可变折射率过渡层可以消除ＳｎＯ↓［２］：Ｆ薄膜的衍射光斑。

Method for preparing refractive index variable transition layer by using zinc fluosilicate

A transition layer with variable refractive index is prepared by using zinc fluosilicate, and the invention belongs to a new type of photoelectron material. In order to solve the SnO: 2: F diffraction pattern of the deposited films in glass and SnO: 2: F layer between a layer of transparent film layer. The invention is mainly used in zinc fluorosilicate, using the method of thermal spray on the surface of glass heating, deposition of SiO decreases, multicomponent film 2 film and SiO down 2 and other metal oxides. The refractive index of the deposited film can be easily adjusted by changing the percentage of the added metal salt in the reaction precursor. The deposition rate of variable refractive transition layer of SnO can be eliminated: 2: diffraction of F thin films.

【技术实现步骤摘要】
一所属
本项专利技术所属领域为，新型材料。二
技术介绍
随着工业化进程步伐的不断加快，工业和日常生活对能源的消耗不断加大；能源消耗对环境的破坏作用也越来越大。能源危机和环境恶化已经成为当今世界不可回避的头等大事。为了解决能源和环境问题，各国争相提出不同的解决方按.有的国家甚至以立法的形式，减少和限制化石能源的消耗，鼓励可再生能源的开发。2005年3月，我国全国人大也颁布了可再生能源法，以法律的形式鼓励节约能源、减少污染排放、增加对新能源的研发投入。在整个能源消耗中，人们的日常生活消耗的能源又占具很大一部分，因此，建筑物的节能是整个节能工作中的非常重要的一个环节。有许多省市已经颁布了建筑物材料节约能源的强制标准。在建筑物中，门窗玻璃的能耗将占整个建筑物的40％。采用新型Low-E玻璃，将明显提高建筑物的节能效果。Low-E玻璃是在普通浮法玻璃表面沉积一层透明氧化物导电薄膜。Badeker于1907年首次报道CdO的透明导电特性，即首次研制出透明导电薄膜(Transparent Conducting Oxide，TCO)。此后，TCO薄膜的研究和应用得到了飞速发展。TCO薄膜除用于太阳本文档来自技高网...

【技术保护点】
用氟硅酸锌（ＺｎＳｉＦ↓［６］．Ｈ↓［２］Ｏ）作为制备ＳｉＯ↓［２］的主要反应前驱液配料，通过热喷涂方式，在加热玻璃表面制备出折射率可变的过渡层。