用作不透明涂层的组合物、带涂层的灯及其制备方法技术

本发明专利技术提供一种用于在玻璃表面上制备不透明银色涂层的组合物。该组合物包括一种至少两种金属粉末的混合物。该金属粉末混合物含有羰基铁和铝，以及一种用于形成金属粉末混合物悬浮液的载液。还提供一种为带玻璃灯罩的灯制备不透明银色涂层的方法。在该方法中，将包括一种羰基铁和铝粉在载液中的混合物的悬浮液涂覆在灯罩上。使悬浮液干燥，随后在高于５００℃的温度下灼烧悬浮液余下的成分。还公开了一种带有玻璃灯罩和覆盖至少一部分玻璃灯罩的单层不透明涂层的灯。该不透明涂层包括５０－８０重量％的羰基铁和２０－５０重量％的元素铝。

Composition for use as an opaque coating, coated lamp and method of making the same

The present invention provides a composition for preparing an opaque silver coating on a glass surface. The composition comprises a mixture of at least two metal powders. The metal powder mixture containing iron and aluminum, and a carrier liquid for forming a metal powder mixture suspension. A method for preparing an opaque silver coating for a lamp with a glass lampshade is also provided. In the method, will include a mixture of iron and aluminum in a carrier liquid suspension coating on the lampshade. The suspension is dried, and the remaining components of the suspension are then fired at temperatures above 500 DEG C. A lamp having a glass chimney and a single layer of opaque coating covering at least a portion of the glass shade is also disclosed. The elements of aluminum opaque coating comprises 50 to 80 wt% of iron and 20 to 50 weight%.

【技术实现步骤摘要】

本专利技术涉及一种用于在玻璃表面，尤其是灯上制备不透明银色涂层的组合物，以及制备这种不透明银色涂层的方法。
技术介绍
现有技术中已知将不透明涂层用于带玻璃灯罩的灯的不同部分。一个典型的例子是覆盖车灯的顶端，来阻止车前灯发出直射(非反射)光线。使车前灯里的灯发出的光以可控的方式投射在路面上，这样可以避免使其他司机晃眼。因此，可以通过金属护罩或者直接涂覆在灯表面的不透明层或涂层，来阻止从灯里向前直射的、不能由投影光学系统控制的光线从灯里逸出。在许多文献，如美国专利US4,305,016和US6,270,237中描述了这种不透明层的使用。例如，美国专利US4,305,016公开了通过使羰基铁和硅粉混和，并进一步形成一种以丁醇作为载液的悬浮液，得到一种用于形成不透明层的合适的组合物。将悬浮液干燥，并对金属粉末混合物进行灼烧来形成一种稳定的、坚硬的、不透明的涂层。然而，该涂层基本上是黑色的。最近，首先由于审美的原因，出现了在灯上使用银色涂层而不是黑色涂层的需求。为了满足这种需求，美国专利US6,270,237中建议在灯上使用双层。建议使用多种金属例如Ag、Al、Ni等，及其混合物来制造具有本文档来自技高网...

【技术保护点】
一种用于在玻璃表面上制备不透明银色涂层（１０）的组合物，包括一种至少两种金属粉末的混合物，该金属粉末混合物含有羰基铁，一种用于形成该金属粉末混合物的悬浮液（２２）的载液，其特征在于，该金属粉末混合物还含有铝。

【技术特征摘要】
...

【专利技术属性】
技术研发人员：I穆德拉，P斯泽梅雷，
申请(专利权)人：通用电气公司，
类型：发明
国别省市：US[美国]