Preparation method of metal oxide arrester non lead sealing glass used first, according to the mass percentage will be 20 ~ 30% V: 2 O: 5, 18 ~ 24% B: 2 O: 3, 45 ~ 55% ZnO, 0 ~ 3% P: 2 O: 5, 0 ~ 10% Bi: 2 O: 3, 0 ~ 5% MO: 3 and 0 ~ 5% BaO mixed evenly; secondly, the batch mixing with corundum crucible at 900 DEG C or a porcelain crucible for melting, melting temperature is 1000 to 1100 DEG C, and the melting temperature of 20 ~ 40 minutes; again, the glass melting liquid good pour in a clean plate cooling; finally, the cooled glass ball into the ball milling tank. The milled glass can be screened with 300 meshes. The invention can be below 530 DEG C and metal oxide arrester firmly sealed together, and does not contain PbO, alkali metal oxides, low melting temperature, low sealing temperature, high resistivity, low expansion coefficient, can be matched with Zinc Oxide seal resistance, high sealing strength.
【技术实现步骤摘要】
本专利技术涉及一种用于陶瓷与ZnO避雷器绝缘子的粘接剂，特别涉及一种金属气化物避雷器用无铅封接玻璃的制备方法。
技术介绍
金属氧化物避雷器的关键部件为氧化锌电阻片。由于氧化锌电阻片易与空气中的潮气反应，从而使其残压值下降，导致避雷器保护性能变差，严重时会造成开裂等故障。为了保证避雷器的安全运行，预防故障发生，采用低熔无铅封接玻璃材料，对氧化锌电阻片之间空隙进行密封封接，防止潮湿的空气进入，起到保护氧化锌电阻片的作用，使避雷器使用寿命提高，达到安全可靠的运行的目的。日本NGK绝缘子(株)专利USP4796149提出了一种与陶瓷和ZnO陶瓷元件有良好热膨胀系数匹配的玻璃，可用于陶瓷与ZnO避雷器绝缘子的粘接，该封接玻璃的PbO含量大于60(wt)％。刘新年等制备了PbO-B2O3-SiO2金属氧化物避雷器用封接玻璃，该封接玻璃的PbO含量大于70(wt)％，其绝缘电阻高，封接温度在500℃左右。另外，V2O5封接玻璃包括V2O5-P2O5，V2O5-TeO2等，该封接玻璃可以在400℃与器件形成气密封接，日立制作所特开平2-267137揭示出了一类适用于LSI外壳...
【技术保护点】
金属氧化物避雷器用无铅封接玻璃的制备方法，其特征在于： １）首先，按质量百分比将２０～３０％的Ｖ↓［２］Ｏ↓［５］，１８～２４％的Ｂ↓［２］Ｏ↓［３］，４５～５５％的ＺｎＯ，０～３％的Ｐ↓［２］Ｏ↓［５］，０～１０％的Ｂｉ↓［２］Ｏ↓［３］，０～５％的ＭＯ↓［３］和０～５％的ＢａＯ混合均匀； ２）其次，在９００℃下的刚玉坩埚或素瓷坩埚中加入该混合均匀的配合料进行熔制，熔制温度为１０００～１１００℃，并在熔制温度下保温２０～４０分钟； ３）再次，将熔制好的玻璃液倒在干净的钢板上冷却； ４）最后，将冷却后的玻璃放入球磨罐中球磨，将球磨后的玻璃过３００目筛即可。
【技术特征摘要】
【专利技术属性】
技术研发人员：郭宏伟，刘新年，高档妮，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：61[中国|陕西]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。