人造硅酸盐及其在玻璃生产中的应用制造技术

通过一种方法生产的粒料，该方法包括以下步骤：（１）通过掺混（ａ）二氧化硅，（ｂ）氧化钙和／或氧化镁和水制成一种混合物；（２）由该混合物形成一种粒料，该粒料包含约３％到约１８％的氧化镁，约６％到约３４％的氢氧化钙，约０％到约２７％的碳酸钙，约０％到约２２％的碳酸镁和约４８％到约６０％的硅砂；以及（３）将该粒料干燥以排出水份从而获得在化学反应过程中处理和／或控制破损所需足够的结构强度。（*该技术在2018年保护过期，可自由使用*）

Artificial silicate and its application in glass production

The production method of pellets, the method comprises the following steps: (1) by mixing (a) silica, calcium oxide (b) and / or Magnesium Oxide and water into a mixture; (2) forming pellets from the mixture, the granule comprises about 3% to about 18% of Magnesium Oxide, ca. 6% to about 34% of the calcium hydroxide, calcium carbonate from about 0% to about 27%, about 0% to about 22% of the magnesium carbonate and about 48% to about 60% of the silica sand; and (3) the pellet drying to discharge water to get treatment and / or damage control required enough structural strength in the process of chemical reaction.

【技术实现步骤摘要】

本专利技术涉及一种制备玻璃用的组合物及其生产方法。更具体地说，本专利技术涉及一种用氧化钙和氧化镁、水和硅酸钠以及硅砂制备的碱金属前体材料。该材料特别用于玻璃生产中，并使得能耗降低，而与玻璃生产物料有关的挥发物质则减少。
技术介绍
玻璃可由玻璃形成体形成，而玻璃形成体被玻璃无序网络理论定义为具有重阳离子-氧的键强度大于大约335千焦耳/摩尔的材料。典型的形成体是氧化物如B2O3、SiO2、GeO2、P2O5、As2O5、P2O3、As2O3、Sb2O3、V2O5、Sb2O5、Nb2O5和Ta2O5。氟化物BeF2也能够作形成体。其它成分可与玻璃形成体混合以提供各种不同的作用。这些成分包括玻璃中间体和玻璃调整剂、中间体键强度大约为250-350千焦耳/摩尔，而其可以变为网络的一部分，或不变为网络的一部分；而调整剂键强度小于大约250千焦耳/摩尔，并且其不会变为网络的一部分。典型的调整剂是镓、镁、锂、锌、钙、钠和钾的氧化物。其它的形成体、中间体和调整剂也是众所周知的，在“玻璃”，Kirk-Othmer化工技术百科全书，12卷，第555页(1994年)中对它们均有描述。玻璃的一种形式是含本文档来自技高网...

【技术保护点】
通过一种方法生产的粒料，该方法包括以下步骤：（１）通过掺混（ａ）二氧化硅，（ｂ）氧化钙和／或氧化镁和水制成一种混合物；（２）由该混合物形成一种粒料，该粒料包含约３％到约１８％的氧化镁，约６％到约３４％的氢氧化钙，约０％到约２７％的碳酸钙，约０％到约２２％的碳酸镁和约４８％到约６０％的硅砂；以及（３）将该粒料干燥以排出水份从而获得在化学反应过程中处理和／或控制破损所需足够的结构强度。

【技术特征摘要】
...

【专利技术属性】
技术研发人员：GH范奇尔德，JA霍克曼，
申请(专利权)人：矿业技术有限公司，
类型：发明
国别省市：US[美国]