A manufacturing method of a halogen energy-saving glass, relates to a preparation method of energy-saving building materials, the method is as follows: firstly the analysis of pure anhydrous NaCl and KCl crystal according to the mass ratio of 1: 1.55 mixture; then the mixture of NaCl and KCl with the ordinary glass raw materials according to the mass ratio of 1: 170 to 290 by mixing; the above mixture production method and process system of ordinary flat glass, can be obtained with high reflection function of infrared glass. The invention is suitable for building glass cooling and heat, can replace the traditional window or curtain wall glass, avoid heat conduction and heat radiation, simple manufacture process, easy to obtain raw materials, the cost is low; the product has high infrared reflectivity.
【技术实现步骤摘要】
本专利技术涉及一种建筑节能材料的制备方法,特别涉及一种掺加卤素的高反射玻璃的制作方法。
技术介绍
随着世界性的能源和资源危机的日益加重,人们对建筑节能也越来越重视。建筑散热和吸热中窗玻璃或幕墙玻璃的比重占到普通建筑的10%~30%,因此是需要重点考虑的领域。目前对于玻璃的热传导普遍采用中空玻璃决断。对于玻璃的热辐射一般采用高反射玻璃避免,目前使用的反射玻璃普遍存在成本高、工艺复杂的缺点。
技术实现思路
本专利技术的目的在于克服现有反射玻璃成本高、工艺复杂的缺点,通过不断试验改进,提供一种工艺简单、成本较低、反射效果好的卤素节能反射玻璃的制作方法。该方法以普通玻璃原料为基本原料,以NaCl和KCl粉体为反射功能添加剂,通过高温熔融和降温定型来制作。本专利技术的目的是通过以下技术方案实现的,其制作方法是先将分析纯的无水NaCl与KCl晶体按质量比1∶1.55混合;再将NaCl和KCl的混合物与普通玻璃原料按质量比1∶170~290混合;按普通平板玻璃的生产方法和工艺制度对以上混合物进行加工,即可得到具有对红外线具有高反射功能的玻璃。本专利技术的优点与效果是本专利技术以普通玻璃原料为基本原料,以NaCl和KCl粉体为反射功能添加剂,其原料容易获得,制作工艺简单,成本较低廉;产品反射效果好。具体实施例方式实施例1将分析纯的无水NaCl与KCl晶体按质量比1∶1.55混合,将NaCl和KCl的混合物与普通玻璃原料按质量比1∶170混合。按普通平板玻璃的生产方法和工艺制度对以上混合物进行加工,即可得到具有对红外线具有高反射功能的玻璃,这种反射膜对红外线的反射率为75% ...
【技术保护点】
一种卤素节能玻璃的制作方法,其特征在于其制作方法是:先将分析纯的无水NaCl与KCl晶体按质量比1∶1.55混合;再将NaCl和KCl的混合物与普通玻璃原料按质量比1∶170~290混合;按普通平板玻璃的生产方法和工艺制度对以上混合物进行加工,即可得到具有对红外线具有高反射功能的玻璃。
【技术特征摘要】
【专利技术属性】
技术研发人员:王博,刘永健,孙驭,
申请(专利权)人:沈阳建筑大学,
类型:发明
国别省市:89[中国|沈阳]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。