A method of making glass reflective film, and relates to a method for preparing energy-saving building materials, the method is: first analysis of pure anhydrous NaCl and KCl crystal in the ratio of 1 to 1.55 are mixed; then NaCl and KCl mixture to airflow grinding to diameter in 1 ~ 100 nm; 0.3 polyethylene plastic film heating to a thickness of 0.5 mm to 105 + 3 DEG C, and then processed NaCl and KCl mixture powder evenly paving in polyethylene plastic film, make the powder completely cover the surface of the film, the film cooling to room temperature, the removal of powder and film without adhesion, can be energy-saving glass reflective film get. The invention is suitable for building window glass or curtain wall glass cooling and heat, can avoid heat conduction and heat radiation, simple manufacture process, easy to obtain raw materials, the cost is low; the product has high infrared reflectivity.
【技术实现步骤摘要】
本专利技术涉及一种建筑节能材料的制备方法，特别涉及。
技术介绍
随着世界性的能源和资源危机的日益加重，人们对建筑节能也越来越重视。在建筑散热和吸热中，窗玻璃或幕墙玻璃的比重占到普通建筑的10％～30％，因此该领域是需要重点考虑的。目前对于玻璃的热传导普遍采用中空玻璃决断。对于玻璃的热辐射一般采用高反射玻璃或贴反射膜避免，所使用的反射膜普遍存在成本高、工艺复杂的缺点。
技术实现思路
本专利技术的目的在于克服现有反射膜成本高、工艺复杂的缺点，通过不断试验改进，提供一种工艺简单、成本较低、反射效果好的节能玻璃反射膜的制作方法。该方法以聚乙烯薄膜为基材，以NaCl和KCl粉体为反射材料，通过高温粘结而成。本专利技术的目的是通过以下技术方案实现的，其制作方法是先将分析纯的无水NaCl与KCl晶体按质量比1∶1.55混合；再将NaCl和KCl混合物以气流磨加工至粒径在1～100纳米；将0.3～0.5毫米厚度的聚乙烯塑料薄膜加热至105±3℃，再将加工好的NaCl和KCl混合物粉体均匀摊铺在聚乙烯塑料薄膜上，使粉体完全覆盖薄膜表面，将薄膜降温至室温，去除未与薄膜粘连的粉体，即可得到节能玻璃反射膜。本专利技术的优点与效果是本专利技术以聚乙烯薄膜为基材，以NaCl和KCl粉体为反射材料，其原料容易获得，制作工艺简单，成本较低廉，对红外线的反射率高。具体实施例方式实施例1将分析纯的无水NaCl与KCl晶体按质量比1∶1.55混合，将NaCl和KCl混合物以气流磨加工，取粒径在1～10纳米的粉体。将0.3～0.5毫米厚度的聚乙烯塑料薄膜加热至105±3℃，再将加工好的粒径在1～...
【技术保护点】
一种节能玻璃反射膜的制作方法，其特征在于其制作方法是：先将分析纯的无水ＮａＣｌ与ＫＣｌ晶体按质量比１∶１．５５混合；再将ＮａＣｌ和ＫＣｌ混合物以气流磨加工至粒径在１～１００纳米；将０．３～０．５毫米厚度的聚乙烯塑料薄膜加热至１０５±３℃，再将加工好的ＮａＣｌ和ＫＣｌ混合物粉体均匀摊铺在聚乙烯塑料薄膜上，使粉体完全覆盖薄膜表面，将薄膜降温至室温，去除未与薄膜粘连的粉体，即可得到节能玻璃反射膜。
【技术特征摘要】
【专利技术属性】
技术研发人员：王博，孙驭，刘永健，
申请(专利权)人：沈阳建筑大学，
类型：发明
国别省市：89[中国|沈阳]