Method for preparing anti infrared optical glass and relates to a production method of optical glass, the method with ordinary optical glass raw materials as the main raw material, the nano TiO: 2 as additive, the melting of the material in ordinary optical glass; melting glass raw materials in the glass raw material quality from 0.1% to 0.21% nano TiO: 2 powder; nano TiO 2 and glass raw materials, lower the melting and stirring evenly; then melting the mixture of cooling and molding to obtain qualified products. The anti infrared optical glass made by the invention can block more than 70% infrared rays to pass through, and simultaneously does not influence the strength of the glass, the ultraviolet ray, the linearity and the luminous rate, and can be used as the optical lens for the sunglasses or the goggles.
【技术实现步骤摘要】
本专利技术涉及一种光学玻璃的制作方法,特别是涉及一种太阳镜或护目镜用的防红外线光学玻璃的制作方法。
技术介绍
紫外线与红外线可对人体的皮肤、眼睛以及免疫系统等造成伤害,强烈的阳光或者特殊的生产环境中都存在着高强度的紫外线、红外线,长时间处于此种工作环境下,会引起急性角膜炎和结膜炎,慢性白内障等眼疾,还会诱发皮肤癌。目前,人们采用的主要保护手段是佩带太阳镜或者专用的护目镜,但普通的太阳镜或护目镜的镜片只具有防紫外线的功能,对红外线的防护作用很微弱,不能有效的保护眼睛。
技术实现思路
本专利技术的目的在于提供一种在有效防止红外线通过的同时不影响玻璃的强度、防紫外线性和通光率的光学玻璃的制作方法。该方法以普通光学玻璃原料为主要原料,以纳米TiO2为添加剂,采用普通光学玻璃的生产方法生产。本专利技术的目的是通过以下技术方案实现的,其制作方法是先将普通光学玻璃的原料熔化;在熔化的玻璃原料中加入该玻璃原料质量0.1%~0.21%的纳米TiO2粉体;将纳米TiO2与熔化的玻璃原料搅拌均匀;再将熔融的混合物降温、成型,即可得到合格的产品。所述的普通光学玻璃原料为普通工业化生产光学玻璃的原料,纳米TiO2为直径在1~100纳米之间的TiO2粉体。本专利技术的优点与效果是1.本专利技术以普通光学玻璃原料为主要原料,以纳米TiO2为添加剂,可有效防止红外线通过。2.本专利技术采用普通光学玻璃的生产方法生产,其生产工艺简单,原料易得,成本低廉。具体实施例方式实施例1将普通光学玻璃的原料熔化,在熔化的玻璃原料中加入该玻璃原料质量0.1%的纳米TiO2粉体,将纳米TiO2与熔化的玻璃 ...
【技术保护点】
一种防红外线光学玻璃的制作方法,其特征在于其制作方法是:先将普通光学玻璃的原料熔化;在熔化的玻璃原料中加入该玻璃原料质量0.1%~0.21%的纳米TiO↓[2]粉体;将纳米TiO↓[2]与熔化的玻璃原料搅拌均匀;再将熔融的混合物降温、成型,即可得到合格的产品。
【技术特征摘要】
【专利技术属性】
技术研发人员:王博,刘永健,孙驭,
申请(专利权)人:沈阳建筑大学,
类型:发明
国别省市:89[中国|沈阳]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。