Manufacturing method of a glass scratch repairing agent, relates to a production method of repair agent, its production process is as follows: the concentration of dilute phosphoric acid, 20% concentration of sodium 40% hydrofluoric acid solution and solid sodium chloride in the ratio of 1: 0.3 to 0.43: 0.05 mixture, stirring to completely dissolve sodium chloride that is the glass scratch repairing agent. The dilute phosphoric acid and hydrofluoric acid sodium and sodium chloride are industrial grade product of the invention is to dilute phosphoric acid and hydrofluoric acid sodium, sodium chloride as the main raw materials of all kinds of glass products scratch repair has the advantages of low toxicity.
【技术实现步骤摘要】
本专利技术涉及一种修复剂的制作方法，特别是涉及。
技术介绍
玻璃制品尽管硬度很高，但是由于往往暴露在环境之中，所以很容易出现划痕，划痕出现后由于对光线不均匀的折射和反射，会影响玻璃制品的外观。现有的玻璃修复剂一般以氢氟酸为主要原料，而氢氟酸有毒，会污染环境和危害人体建康。
技术实现思路
本专利技术的目的在于克服现有玻璃修复材料毒性大的缺点，通过试验改进，提供一种以稀磷酸和氢氟酸钠、氯化钠为主要原料的低毒性的玻璃划痕修复剂的制作方法。本专利技术的目的是通过以下技术方案实现的，其制作过程为将浓度为20％的稀磷酸、浓度为40％的氢氟酸钠溶液和固态的氯化钠按质量比1∶0.3～0.43∶0.05混合，搅拌，让氯化钠完全溶解，即为玻璃划痕修复剂。如上所述的稀磷酸和氢氟酸钠、氯化钠均为工业级产品。本专利技术的优点与效果是 本专利技术以稀磷酸和氢氟酸钠、氯化钠为主要原料，具有低毒性的优点。具体实施例方式实施例1将浓度为20％的稀磷酸、浓度为40％的氢氟酸钠溶液和固态的氯化钠按质量比1∶0.3∶0.05混合，搅拌，让氯化钠完全溶解。即为玻璃划痕修复剂。将该溶液滴加在普通硅酸盐玻璃表面1分钟内可以溶解0.0170毫米厚的玻璃。实施例2将浓度为20％的稀磷酸、浓度为40％的氢氟酸钠溶液和固态的氯化钠按质量比1∶0.32∶0.05混合，搅拌，让氯化钠完全溶解。即为玻璃划痕修复剂。将该溶液滴加在普通硅酸盐玻璃表面1分钟内可以溶解0.0177毫米厚的玻璃。实施例3将浓度为20％的稀磷酸、浓度为40％的氢氟酸钠溶液和固态的氯化钠按质量比1∶0.43∶0.05混合，搅拌，让氯化钠完全溶...
【技术保护点】
一种玻璃划痕修复剂的制作方法，其特征在于其制作过程为：将浓度为２０％的稀磷酸、浓度为４０％的氢氟酸钠溶液和固态的氯化钠按质量比１∶０．３～０．４３∶０．０５混合，搅拌，让氯化钠完全溶解，即为玻璃划痕修复剂。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。