A porous glass preparation method, the waste glass powder, manganese dioxide, ferric oxide and boric acid; then adding polyvinyl alcohol and distilled water polo ground into paste; the foamed plastic into the slurry, the plastic foam sponge all immersed in the slurry, put out on the refractory material, and into the foaming kiln, drying, sponge foaming and foam stability combustion, cooling and annealing to obtain porous glass. The porous foamed glass is prepared by using industrial waste material as raw material, adding a small amount of additive, and taking foam sponge as bubble forming agent and adopting sponge dipping method. Not only conducive to the use of waste, protect the environment, and the prepared porous glass through hole rate of more than 90%, light weight, high strength, uniform pore size distribution, can be used as sound-absorbing materials and special filter materials good.
【技术实现步骤摘要】
本专利技术涉及一种泡沫玻璃的制备方法，特别涉及一种。
技术介绍
泡沫玻璃是利用废弃玻璃为主要原料，添加发泡剂、改性剂、促进剂等经细粉碎和均匀混合成配合料，放置在特定模具中经过750～900℃温度加热，使玻璃软化、发泡、退火形成一种内部充满无数均匀气泡的多孔玻璃材料。泡沫玻璃具有密度小、强度高、导热系数小等物理性质，其不仅具有玻璃材料本身固有的永久性、安全性、可靠性、防化学腐蚀性和不受蚁鼠侵害等优点，而且与其它建筑材料相比，还具有保温隔热、防水防潮、防火、耐酸碱、密度小、机械强度高、吸声等一系列优越性能。近年来，随着对泡沫玻璃应用方面的进一步研究和开发，发现泡沫玻璃在作为吸声材料和过滤材料方面具有很多优点，比如体积密度小，强度高，导热系数小等。但是，泡沫玻璃的开孔气孔率为2％～20％。当泡沫玻璃作为吸声材料和特种过滤材料时，我们希望泡沫玻璃开孔气孔率，尤其是连通气孔的开孔气孔率越高越好，一般常采用特殊的发泡剂来制备开孔气孔率较高的泡沫玻璃，但开孔气孔率的提高幅度也有限。文献CN2358074Y中报道了一种高效吸声泡沫玻璃，通过在泡沫玻璃的迎声面和及迎声面的对面采...
【技术保护点】
一种通孔泡沫玻璃制备方法，其特征在于：１）首先，将废平板玻璃清洗干净，烘干后球磨至３００目，然后按质量分数将球磨后的９５％的玻璃粉，１．５％的二氧化锰，１．５％三氧化二铁和２．０％硼酸放入球磨罐中制成配合料；２）其次，在球磨 罐中再加入配合料质量３～５％的聚乙烯醇和８％的蒸馏水球磨５～１０小时制成浆料；３）将密度为２０～４０ｋｇ／ｍ↑［３］的塑料泡沫海绵浸入到料浆中，待塑料泡沫海绵中全部浸入料浆后，取出放于耐火材料上，并移入发泡窑中，按照以下烧成制度烧成 ：干燥阶段，升温速度为３℃／ｍｉｎ，升温至１５０℃，保温２～３小时；海绵燃烧...
【技术特征摘要】
【专利技术属性】
技术研发人员：郭宏伟，高档妮，高淑雅，刘新年，赵彦钊，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：61[中国|陕西]