The invention discloses a method for preparing B tungstate nano film, which comprises the following steps: A. according to the molar ratio of 1 and 1 respectively weighing II B metal salt and tungsten source, the autoclave in 140 ~ 200 DEG C and heated for 2 to 12 hours; after centrifugation to precipitate B., adding alcohol, stir with collodion, stirring; C. coating substrate processing standby; D. coating after 150 ~ 200 DEG C for 350 to 30 minutes, the constant temperature of 500 DEG C for 1 hours, then slowly to room temperature, to obtain the product of the invention. The invention is a new method of hydrothermal and collodion dispersing nanoparticles into the membrane technique, high yield of 90%, the prepared product has good optical and electrical properties, has obvious blue shift of emission peak. The invention has the advantages of easy availability of raw materials, low cost, simple operation, convenient treatment and easy industrialization.
【技术实现步骤摘要】
本专利技术涉及一种纳米薄膜的制备方法，特别是涉及一种通过水热法和 胶棉分散纳米粒子成膜技术相结合的制备IIB族钨酸盐纳米薄膜的方法。
技术介绍
IIB族钩酸盐粉体材料由于其独特的闪烁和发光特性等而在光学、电 子、生物、涂料、医药等行业具有广阔的应用前景。研究证实，当粉体材 料被加工成薄膜时，由于薄膜材料固有的小尺寸和低的横向散射等特点， 使得无机发光薄膜材料具有较其粉体材料更加优异的光、电、磁、催化等 性能，可用于固态激光、光纤维、发光闪烁体、加速器等领域。随着光电 器件微型化的要求，纳米薄膜材料在整个新材料的研究应用方面日益引起 人们的广泛关注。迄今，已报道的IIB族钨酸盐纳米薄膜的制备方法主要 有溶胶-凝胶法、溅射法、水热-溶剂热合成法和电化学法。然而上述制 备方法都不同程度的存在有制备成本高，易产生有毒气体、产物形貌难以 控制等问题，不能满足生产光电器件的需求。 一般而言，水热法能从微观 上稳定微粒并控制粒子的尺寸和形貌又具有高产率优势，可进行规模生产， 然而到目前为止，尚未见到以水热体系和胶棉分散纳米粒子成膜技术相结 合制备IIB族钨酸盐纳米薄膜的报道。...
【技术保护点】
ⅡＢ族钨酸盐纳米薄膜的制备方法，包括下列步骤： ａ．按照摩尔比１∶１的比例分别称取ⅡＢ族金属盐和钨源，将其置入到带有聚四氟乙烯内衬的高压釜中，往高压釜中添加蒸馏水至高压釜容积的２／３，然后封闭高压釜并将其置于烘箱中１４０～２００℃加热２～１２小时，反应结束后将高压釜梯度冷至室温，其中所述的ⅡＢ族金属盐选自可溶性的ⅡＢ族金属氯酸盐、硝酸盐或醋酸盐中的一种，所述的钨源选自Ｎａ↓［２］ＷＯ↓［４］、Ｋ↓［２］ＷＯ↓［４］或Ｈ↓［２］ＷＯ↓［４］中的一种； ｂ．将步骤ａ高压釜中的沉淀产物离心分离后，依次用蒸馏水、丙酮和无水乙醇分别清洗三次，再向其中加入沉淀产物体积０．２...
【技术特征摘要】
【专利技术属性】
技术研发人员：贾润萍，何新耀，王霞，欧阳春发，杨俊和，
申请(专利权)人：上海应用技术学院，
类型：发明
国别省市：31[中国|上海]