制作玻璃光纤预制棒的方法技术

原材料气体，燃烧气体，和载体气体被输送到芯沉积燃烧器中，而原材料气体，燃烧气体，载体气体，和用于掺氟的气体被输送到包层沉积燃烧器中，从而形成由芯玻璃粉尘棒和包层玻璃粉尘棒构成的多孔玻璃粉尘棒。随着粉尘棒的生长，增加掺氟气体供给量同时保持其它气体供给量不变。接着，进行粉尘棒的去氢和透明化过程。按此法制作出来的是，具有低浓度氟并在生长方向上有高均匀度的石英玻璃部分的玻璃光纤预制棒。（*该技术在2016年保护过期，可自由使用*）

Method for making glass fiber preform

The raw material gas, combustion gas, and carrier gas are supplied to the core sediments in the burner, and raw material gas, combustion gas, carrier gas, and gas for fluorine doped cladding deposition is transported to the burner, which is composed of core and cladding glass glass soot dust bar in a porous glass soot. With the growth of the dust rod, the supply of fluorine gas is increased while the other gas supply is kept unchanged. Then, the process of hydrogen removal and transparency of the dust rod is carried out. The glass fiber preform which has a low concentration of fluorine and has a high uniformity of quartz glass in the direction of growth is fabricated by this method.

【技术实现步骤摘要】

本专利技术涉及一种具有掺氟石英玻璃部分的玻璃光纤预制棒的制作方法，它具有一个用汽相轴向沉积(VAD)法沉积玻璃细粒子的步骤。光纤具有芯和环绕着芯而折射率比芯低的包层这样一种结构。靠着芯与包层的折射率之间的差别，光被聚拢在芯的内部或附近传播。于是，为了实现光纤的功能，提高或降低折射率的掺杂物被加入到基质材料中，由此实现所需的折射率分布。如果基质材料是石英玻璃，氟适于作为降低折射率的一种掺杂物。具有掺氟石英玻璃部分的光纤，通过加热位伸有掺氟石英玻璃部分的光纤预制棒而制出。这样的玻璃光纤预制棒，至今如下文所述被制作出来。形成掺氟石英玻璃部分的第一种传统方法(下文称为传统实例1)，是如日本专利公开62-38292所公开的那种，其方式是为了用VAD法生长出细玻璃粒子体，供给玻璃原材料气体和燃烧气体，并沿着靶轴的方向用火焰水解法沉积出玻璃粒子，且随后在氟化物气体中进行玻璃粒子固化步骤，从而得到有掺氟玻璃部分的玻璃光纤预制棒。形成掺氟石英玻璃部分的第二种传统方法(下文称为传统实例2)，是如日本专利申请公开59-232934所公开的那种，其方式是为了用VAD法生长出细玻璃粒子体，供给玻璃原材料本文档来自技高网...

【技术保护点】
一种制作具有用汽相轴向沉积法掺杂氟的石英玻璃部分的玻璃光纤预制棒的方法，包括： 第一步，将玻璃原材料气体和氟化物气体引入氧焰中并通过火焰水解在靶轴方向上沉积精细的玻璃微粒，从而让所述的精细玻璃微粒沉积体沿着所述的靶轴方向生长，其中所述精细玻璃微粒沉积体的生长周期包含增加所供给的氟化物气体流速的周期，和 第二步，加热透明化所述的精细玻璃微粒沉积体。

【技术特征摘要】
...

【专利技术属性】
技术研发人员：石川真二，伊藤真澄，星野寿美夫，
申请(专利权)人：住友电气工业株式会社，
类型：发明
国别省市：JP[日本]