浮法玻璃及其制作方法以及利用该浮法玻璃的显示器面板技术

本发明专利技术提供适用于ＰＤＰ等显示器面板的、纵向的热收缩率和横向的热收缩率之差极小的浮法玻璃及其制作方法、以及利用该浮法玻璃的显示器面板。所述浮法玻璃是通过浮法制作的浮法玻璃，其特征在于，该玻璃按以下条件热处理后，纵向和横向的热收缩率之差为±５ｐｐｍ以下，热处理条件为，从常温以１０℃／分钟的速度升温至６００℃，在６００℃放置３０分钟后，以１０℃／分钟的速度降温至常温。

Float glass and method for making the same, and display panel using the float glass

The present invention provides a float glass suitable for a display panel of PDP, such as a longitudinal heat shrinkage rate and a transverse heat shrinkage rate, and a manufacturing method thereof, and a display panel using the float glass. The float glass is produced by the float glass float, which is characterized in that the glass according to the following conditions after heat treatment, heat shrinkage rate of vertical and horizontal deviation was below 5ppm, the heat treatment conditions, from room temperature to 10 DEG C / min speed up to 600 DEG C for 30 minutes on the 600 C, 10 C / min speed cooling to room temperature.

【技术实现步骤摘要】

本专利技术涉及浮法玻璃及其制作方法，具体地说涉及适用于等离子显示器等显示器面板的浮法玻璃及其制作方法以及利用该浮法玻璃的显示器面板。
技术介绍
玻璃是非晶体，具有无规则的原子排列结构，所以把玻璃加热到某一温度以上时，结构就会在该温度中向最稳定的状态变化、即叫做结构缓和的现象。在产生该结构缓和的温度区域，玻璃产生热变形，冷却至室温后有时不能恢复到原来形状。作为等离子显示器面板(以下称“PDP”)等的基板所用的玻璃基板，在面板制作过程中，有必要把玻璃加热到产生结构缓和的温度区域，而冷却后由于结构缓和有时会产生热收缩问题。也就是，PDP等的制作是，将指定形状的电极与设置在其表面的两张玻璃基板精密对齐连接，使电极图案没有偏离，但是此时由于玻璃基板的热收缩，有时会产生电极图案的偏离。因此需要解决这个问题。作为减少玻璃基板的热收缩的方法，已提出过几种方法。例如，在浮法玻璃的制作方法中，将熔融玻璃拉伸，形成带状玻璃，将该带状玻璃从熔融锡分离的温度TO和该浮法玻璃的玻璃化温度TG之间关系中，将TO控制在TG-50℃～TG+30℃范围(参照专利文献1，权利要求书)。另外，还提出过，在玻璃的加热工艺本文档来自技高网...

【技术保护点】
一种浮法玻璃，它是通过浮法制作的浮法玻璃，其特征在于，该玻璃按以下条件热处理后，纵向和横向的热收缩率之差为±５ｐｐｍ以下，　　　　热处理条件：从常温以１０℃／分钟的速度升温至６００℃，在６００℃放置３０分钟后，以１０℃／分钟的速度降温至常温。