Method for treating lead containing wastewater by modified wheat lees. The invention uses grains as the main raw material, soaking wheat using Sodium Chloride Solution 0.5 - 2mol / L 8 - 15 hours of bad modification, the modified grains added to the waste water treatment of lead, 1 ~ 6 hours after adsorption, adsorption, supernatant discharge. The invention makes full use of industrial waste beer spentgrains as adsorbent for adsorption of lead wastewater, truly realize the \bywaste\; and the realization of clean, efficient and inexpensive treatment of wastewater containing lead, reaches the national standard of stable lead ion in water, lead to lead wastewater treatment with 1 - 100mg / L after the lead content in water as low as 0.09mg / L0.52mg / L, far below the standards of 1mg / L.
【技术实现步骤摘要】
本专利技术涉及一种含铅废水处理方法，特别是涉及一种采用改性麦糟处理含铅废水使含铅废水稳定达到《污水综合排放标准》(GB8978—1996) 的方法，属于环境工程领域。
技术介绍
目前工业生产上和铅有关的行业己经有三、四百种。而铅是有 毒金属，铅和可溶性铅盐均有毒，铅被人体吸收后主要损害骨骼造血系统和神 经系统，引发造血、神经、消化、泌尿系统等一系列病症。因此，消除废水 中的铅对环境保护和人体健康具有十分重要的意义。目前工业上一般采用化学沉淀法和离子交换法处理废水中重金属铅离子。 而电解法则是一种有待人们重新认识的古老而全新的方法。另外，液膜法和生 物吸附法是新兴的含铅废水的处理方法，目前处于研究阶段。化学沉淀法所用沉淀剂有石灰、烧碱、氢氧化镁、纯碱以及磷酸盐。其中 氢氧化物沉淀法应用较多。但大量的含铅污泥不易处理，容易造成二次污染，且 化学沉淀法有占地面积大、处理量小、选择性差等缺点。离子交换法处理铅离子 是较为理想的方法之一，不但占地面积小、管理方便、铅离子脱除率很高，而且 处理得当可使再生液作为资源回收，不会对环境造成二次污染，缺点是离子交换 法的一次性投资...
【技术保护点】
改性麦糟处理含铅废水的方法，其特征在于：采用０．５－２ｍｏｌ／Ｌ的氯化钠溶液浸泡麦糟８－１５小时进行改性，改性后经洗涤、干燥、研碎、过２７０μｍ筛，得到改性麦糟吸附剂；调节含铅废水ｐＨ值为４．５～６．５，将改性麦糟与含铅废水按质量体积比２～１０ｇ／Ｌ的比例混合，进行１～６小时的吸附，吸附处理后，上清液达标排放。
【技术特征摘要】
【专利技术属性】
技术研发人员：柴立元，李青竹，王云燕，舒余德，闵小波，彭兵，杨志辉，王海鹰，黄燕，陈云嫩，
申请(专利权)人：中南大学，
类型：发明
国别省市：43[中国|湖南]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。