The invention provides a multifunctional zinc-iron alloy electroplating solution and a preparation method thereof, which belongs to the technical field of electroplating. It mainly contains main salt, stabilizer, complexing agent, cathode activator, accelerator and reductant needle. Its pH value is 9.0-11.0. The invention solves the problems of the existing galvanizing process, poor covering and dispersing ability of the galvanizing solution, and provides a multi-functional galvanizing solution of zinc-iron alloy by adding reducing agent in the galvanizing bath. The electroplating solution has the advantages of strong covering and dispersing ability, and can be widely used in the galvanizing process of printed circuit boards, electromagnetic wave sealing and inner hole wall of tubular parts.
【技术实现步骤摘要】
一种多功能锌铁合金电镀溶液及其制备方法
本专利技术涉及一种电镀技术,具体是指一种多功能锌铁合金电镀溶液及其制备方法。
技术介绍
锌铁合金由于本身具有优良的导电性及传热性,是目前使用最普遍的镀种之一。现有的电镀锌工艺,存在镀液的覆盖能力和分散能力差的问题。近几年盛行研究甲醛溶液的替代物用作镀锌液中的还原剂,专利技术一种覆盖能力和分散能力更好的镀液具有非常重要的意义。
技术实现思路
本专利技术提供一种多功能锌铁合金电镀溶液及其制备方法,这种新的电镀方法,镀液具有优良的分散能力和覆盖能力。本专利技术的技术方案是这样实现的:一种多功能锌铁合金电镀溶液,主要包含主盐、稳定剂、络合剂、阴极活化剂,促进剂和还原剂;所述电镀液的pH值为9.0~11.0;其中:所述还原剂为次亚磷酸钠,其含量为30~50克/升。所述主盐为硫酸锌,含量为60~80克/升所述阴极活化剂为氯离子。所述促进剂为硫酸镍、硫酸钴中的一种或两种。PH用氨水或硫酸调整。一种多功能锌铁合金电镀溶液的电镀方法,其特征在于包括以下步骤:(1)将锌铁合金放入上述的功能性锌的电镀溶液中,作为阳极;(2)将工件放入上述的功能性锌的电镀溶液中,作为阴极;(3)通入直流电源,阴极电流密度0.2~2安培/平方分米,电镀液温度45~60℃,电镀时间2~10分钟。所述步骤(3)中阴极电流密度为0.5~1.5安培/平方分米;电镀液温度为50~55℃;电镀时间为5~8分钟。与现有技术相比,本专利技术具有的有益效果为:1)通过在镀液中加入还原剂,可显著提高镀液的覆盖能力。2)通过在镀液中加入还原剂,可明显提高镀液的分散能力。具体实施方式下 ...
【技术保护点】
1.一种多功能锌铁合金电镀溶液,主要包含主盐、稳定剂、络合剂、阴极活化剂,促进剂和还原剂;所述电镀液的pH值为9.0~11.0;其中:
【技术特征摘要】
1.一种多功能锌铁合金电镀溶液,主要包含主盐、稳定剂、络合剂、阴极活化剂,促进剂和还原剂;所述电镀液的pH值为9.0~11.0;其中:2.如权利要求2所述的一种多功能锌铁合金...