The invention discloses a wear-resistant magnesium alloy coating, which comprises a metal substrate and a corrosion-resistant coating. The metal substrate is magnesium alloy. The composition and weight components of the corrosion-resistant coating are 60 70 parts of manganese powder, 8 12 parts of iron powder, 1.5 2.5 parts of sodium carboxymethyl cellulose, 0.5 1 part of organic acid, 0.5 1 part of defoamer, 18 parts of water, and manganese powder, iron powder and water. The slurry is prepared by premixing sodium carboxymethyl cellulose, adding organic acid, defoamer and water after grinding, and then the corrosion resistant coating is prepared by coating process. Through the above method, the invention has good adhesion, corrosion resistance and protection performance to the matrix, and the manufacturing process is simple, safe and environmental protection.
【技术实现步骤摘要】
一种耐磨损镁合金涂料的制备工艺
本专利技术涉及金属涂层领域,特别是涉及一种耐磨损镁合金涂料。
技术介绍
现代科学和技术的发展,工业生产对材料性能的要求愈来愈高。由于工程机械等工作条件日益苛刻,要求材料具有耐腐蚀、耐磨损等性能,以致单纯的金属材料难以满足要求。涂层是指附着在某一基体材料上起某种特殊作用,且与基体材料具有一定结合强度的薄层材料。它可以克服基体材料的某种缺陷,改善其表面特性,如光学特性、电学特性、耐侵蚀及腐蚀、耐磨损性和提高机械强度等,它属于一种有支撑体的薄膜。镁及其合金属于轻质金属结构材料,被广泛运用于汽车制造、航空航天、家电、手机等产品的制造,但镁的化学非常活泼,极易发生腐蚀,因此,对镁合金材料表面附着一层耐腐蚀金属涂层,以提高其耐腐蚀性就显得迫为需要。
技术实现思路
本专利技术主要解决的技术问题是提供一种耐磨损镁合金涂料,具有良好的结合力、耐腐蚀性以及对基体的防护性能,且制造工艺简单、安全环保。为解决上述技术问题,本专利技术采用的一个技术方案是:提供一种耐磨损镁合金涂料,包括:金属底材和耐腐蚀涂层,所述金属底材为镁合金,所述耐腐蚀涂层的成分及其重量份数为:锰粉60-70份、铁粉8-12份、羧甲基纤维素钠1.5-2.5份、有机酸0.5-1份、消泡剂0.5-1份、水18-25份,所述配方量的锰粉、铁粉和羧甲基纤维素钠预混合、研磨后加入配方量的有机酸、消泡剂和水制得浆料,然后经涂装工艺制得所述耐腐蚀涂层。在本专利技术一个较佳实施例中,所述涂装工艺流程为:金属底材表面抛光、去油脂处理—水洗—浸涂或喷涂浆料—常温干燥—高温烘烤。在本专利技术一个较佳实施例 ...
【技术保护点】
1.一种耐磨损镁合金涂料,其特征在于,包括:金属底材和耐腐蚀涂层,所述金属底材为镁合金,所述耐腐蚀涂层的成分及其重量份数为:锰粉60‑70份、铁粉8‑12份、羧甲基纤维素钠1.5‑2.5份、有机酸0.5‑1份、消泡剂0.5‑1份、水18‑25份,所述配方量的锰粉、铁粉和羧甲基纤维素钠预混合、研磨后加入配方量的有机酸、消泡剂和水制得浆料,然后经涂装工艺制得所述耐腐蚀涂层。
【技术特征摘要】
1.一种耐磨损镁合金涂料,其特征在于,包括:金属底材和耐腐蚀涂层,所述金属底材为镁合金,所述耐腐蚀涂层的成分及其重量份数为:锰粉60-70份、铁粉8-12份、羧甲基纤维素钠1.5-2.5...