The invention discloses a polyester knitted fabric, which comprises a body with a water absorbent coating on its surface and a coil structure interwoven with 16.7 tex polyester yarn. The length of the coil of the polyester yarn is 24.5 cm/100 needles. The polyester yarn is twisted by polyester monofilament. The cross section of the polyester monofilament is trifoliate. The polyester monofilament has three uniformly dispersed blades and four polyester monofilaments are arranged on the body. Three through holes are located in the middle of each blade, and the other one is located at the junction of three blades. The weight of knitted fabric is 130 g/m2. The polyester knitted fabric of the invention can absorb moisture and sweat and has good water absorption.
【技术实现步骤摘要】
涤纶针织布
本专利技术涉及针织织物
,尤其是涉及一种涤纶针织布。
技术介绍
涤纶是一种非常常见的合成纤维,由于其具有极其优良的定形性能,因此被大量地用于制造衣着面料。涤纶织物定形后,在使用中经过多次洗涤,仍然能保持原有形状。此外,它还具有强度高、弹性好、耐热、耐腐蚀等等优点。然而涤纶的透气性、吸湿性较差,由其制成的服装在长时间穿着后,湿气不易散发,容易产生臭味,同时对涤纶布料的吸水性也有待改进。
技术实现思路
本专利技术的目的在于克服上述现有技术的不足,提供一种吸水性好,吸湿排汗的涤纶针织布。为达到上述目的,本专利技术的技术方案是:涤纶针织布,包括本体,所述本体的表面设有吸水涂层,本体具有16.7tex的涤纶纱交织成的线圈结构,所述涤纶纱的线圈长度为24.5cm/100针,涤纶纱由涤纶单丝加捻而成,所述涤纶单丝的截面为三叶型,涤纶单丝具有三个向外均匀发散的叶片,涤纶单丝上设有四个通孔,其中三个通孔分别位于每个叶片的中间处,另外一个通孔位于三个叶片的交界处,所述针织布的克重为130克/平方米。所述吸水涂层为高分子吸水树脂涂层,其厚度为0.01mm~0.03mm。本专利技术的有益效果是:吸水涂层使得本专利技术具备超强的吸水能力,三叶型的涤纶单丝及其内部的通孔的设置,形成了汗水湿气导流的毛细孔道,大大提升了吸湿排汗性。附图说明图1为本专利技术的结构示意图;图2为本专利技术的本体的局部编织图;图3为本专利技术的涤纶单丝的截面图。图中:本体1、吸水涂层2、涤纶纱3、叶片4、通孔5。具体实施方式下面通过实施例,并结合附图,对本专利技术的技术方案作进一步具体的说明。如 ...
【技术保护点】
1.涤纶针织布,包括本体(1),其特征在于:所述本体(1)的表面设有吸水涂层(2),本体(1)具有16.7tex的涤纶纱(3)交织成的线圈结构,所述涤纶纱(3)的线圈长度为24.5cm/100针,涤纶纱(3)由涤纶单丝加捻而成,所述涤纶单丝的截面为三叶型,涤纶单丝具有三个向外均匀发散的叶片(4),涤纶单丝上设有四个通孔(5),其中三个通孔(5)分别位于每个叶片(4)的中间处,另外一个通孔(5)位于三个叶片(4)的交界处,所述针织布的克重为130克/平方米。
【技术特征摘要】
1.涤纶针织布,包括本体(1),其特征在于:所述本体(1)的表面设有吸水涂层(2),本体(1)具有16.7tex的涤纶纱(3)交织成的线圈结构,所述涤纶纱(3)的线圈长度为24.5cm/100针,涤纶纱(3)由涤纶单丝加捻而成,所述涤纶单丝的截面为三叶型,涤纶单丝具有三个向外均匀发散的叶片...
【专利技术属性】
技术研发人员:高建芬,
申请(专利权)人:绍兴柯桥名瑶纺织品有限公司,
类型:发明
国别省市:浙江,33