The invention discloses a high-strength thermoplastic rubber, which comprises 40 to 50 copies of styrene-based thermoplastic elastomer, 45 to 50 copies of heavy calcium carbonate, 3 to 5 copies of black masterbatch, 7 to 10 copies of polypropylene, 5 to 10 copies of white oil, 1.5 to 2.0 copies of coupling agent, 1 to 3 copies of reinforcing filler, 0.5 to 1.0 copies of smoothing agent and 1 to 3 copies of tackifier by weight. The reinforcing filler comprises 10 copies of silicon oxide by weight. 40 copies, 20 30 copies of alumina, 20 30 copies of calcium oxide, 20 30 copies of titanium oxide, 5 10 copies of antimony oxide and 5 15 copies of boron nitride. The high-strength thermoplastic rubber obtained by the invention improves the strength and anti-aging ability of the thermoplastic rubber through appropriate proportion, and the cost is reduced by choosing heavy calcium carbonate as filler.
【技术实现步骤摘要】
一种高强度的热塑性橡胶
本专利技术涉及一种橡胶材料，特别是一种高强度的热塑性橡胶。
技术介绍
热塑性橡胶是一种兼具橡胶和热塑性塑料特性的材料，由于其双重性能和宽广的特性，使之在橡胶工业中广泛用于制造胶鞋、胶布等日用制品和胶管、胶带、胶条、胶板、胶件以及胶粘剂等各种工业用品。目前市面上的热塑性橡胶其稳定程度不高，主要是易老化和强度不够。
技术实现思路
本专利技术的目的是为了解决上述现有技术的不足而提供一种配方合理、高强度的热塑性橡胶。为了实现上述目的，本专利技术所设计的一种高强度的热塑性橡胶，按重量配比份包括40-50份苯乙烯系热塑性弹性体、45-50份重质碳酸钙、3-5份黑色母粒、7-10份聚丙烯、5-10份白油、1.5-2.0份偶联剂、1-3份增强填料、0.5-1.0份光滑剂和1-3份增粘剂，所述增强填料按重量份包括氧化硅10-40份、氧化铝20-30份、氧化钙20-30份、氧化钛20-30份、氧化锑5-10份和氮化硼5-15份。苯乙烯系热塑性弹性体是苯乙烯-丁二烯-苯乙烯三段共聚物，具有优良的拉伸强度和弹性，永久变形小，屈挠和回弹性好，表面摩擦大。重质碳酸钙重质碳酸钙作为无机填料，具有化学纯度高、惰性大、不易化学反应、分散性好等优点。偶联剂、增强填料、光滑剂和增粘剂等助剂主要起到提高橡胶与固体表面粘合强度的作用，并可以增强耐磨、耐老化性能。本专利技术得到的一种高强度的热塑性橡胶，通过合适的配比，实现了热塑性橡胶的强度和防老化能力的提升，填充物选用重质碳酸钙则降低了成本。具体实施方式下面结合实施例对本专利技术进一步说明。实施例1：本专利技术提供的一种高强度的...
【技术保护点】
1.一种高强度的热塑性橡胶，其特征在于：按重量配比份包括40‑50份苯乙烯系热塑性弹性体、45‑50份重质碳酸钙、3‑5份黑色母粒、7‑10份聚丙烯、5‑10份白油、1.5‑2.0份偶联剂、1‑3份增强填料、0.5‑1.0份光滑剂和1‑3份增粘剂，所述增强填料按重量份包括氧化硅10‑40份、氧化铝20‑30份、氧化钙20‑30份、氧化钛20‑30份、氧化锑5‑10份和氮化硼5‑15份。
【技术特征摘要】
1.一种高强度的热塑性橡胶，其特征在于：按重量配比份包括40-50份苯乙烯系热塑性弹性体、45-50份重质碳酸钙、3-5份黑色母粒、7-10份聚丙烯、5-10份白油、1.5-2.0份偶联剂、1-...