The invention discloses a chlorinated polyvinyl chloride elastic material and its preparation method and application. The chlorinated polyvinyl chloride elastic material includes 100 parts of polyvinyl chloride, 20 30 parts of polyether ether ketone, 10 40 parts of reinforced fiber, 1 2 parts of polyphenylene sulfone, 0.5 1 part of coupling agent and 1 2 parts of additives. The elastic material of chlorinated polyvinyl chloride can be used to prepare pipes or plates for chemical industry. The beneficial effect of the invention is that the obtained product not only keeps the original performance of chlorinated polyvinyl chloride, but also greatly improves the impact resistance and elasticity, widens the application field and has good market prospect.
【技术实现步骤摘要】
氯化聚氯乙烯弹性材料及其制备方法和应用
本专利技术涉及一种功能性氯化聚氯乙烯及其制备方法和应用。
技术介绍
氯化聚氯乙烯(CPVC)因为拥有良好的耐腐蚀、耐温、耐候、阻燃等特性,被广泛的用于制备各种化工材料,包括化工管道以及板材。同时,由于CPVC树脂具有难燃、耐油、耐化学药品腐蚀、耐水等特性,同样非常适合用来替代PVC软管。但是,常规的氯化聚氯化氯乙烯材料,也存在抗冲击性和弹性还不够理想的缺陷,不能满足相关领域应用的需要。
技术实现思路
本专利技术的目的是公开一种聚氯化氯乙烯弹性材料及其制备方法和应用,以克服现有技术存在的缺陷。所述的氯化聚氯乙烯弹性材料,包括如下重量份数的组分:优选的,所述的氯化聚氯乙烯弹性材料,包括如下重量份数的组分:所述聚醚醚酮的熔融指数为20~200g/10min、数均分子量(Mn)为20000~39000中的一种或几种的组合物。所述聚亚苯基砜的熔融指数为12~40g/10min,优选19~30g/10min。所述增强纤维为玻璃纤维或碳纤维,玻璃纤维含量为20~70%,碳纤维含量为20~40%;所述的偶联剂选自硅烷偶联剂、钛酸酯偶联剂或两者复配,优选硅烷偶联剂,可采用商业化产品SG-Si900,如A-1120、Z-6020、KBM-603等;所述添加剂包括抗氧剂、高温润滑剂、抗静电剂、着色剂或脱模剂等中的一种以上;所述抗氧剂为受阻酚类抗氧剂,如N,N'-双-[3-(3,5-二叔丁基-4-羟基苯基)丙酰基]己二胺(抗氧剂1098);所述高温润滑剂为乙烯丙烯酸共聚物、硅酮粉,聚有机硅氧烷等;所述的氯化聚氯乙烯弹性材料的制备方法,包括以下步 ...
【技术保护点】
1.氯化聚氯乙烯弹性材料,其特征在于,包括如下重量份数的组分:
【技术特征摘要】
1.氯化聚氯乙烯弹性材料,其特征在于,包括如下重量份数的组分:2.根据权利要求1所述的氯化聚氯乙烯弹性材料,其特征在于,包括如下重量份数的组分:3.根据权利要求1或2所述的氯化聚氯乙烯弹性材料,其特征在于,所述聚醚醚酮的熔融指数为20~200g/10min、数均分子量(Mn)为20000~39000中的一种或几种的组合物。4.根据权利要求1或2所述的氯化聚氯乙烯弹性材料,其特征在于,所述聚亚苯基砜的熔融指数为12~40g/10min。5.根据权利要求1或2所述的氯化聚氯乙烯弹性材料,其特征在于,所述增强纤维为玻璃纤维或碳纤维。6.根据权利要求1或2所述的氯化聚氯乙烯弹性材料,其特征在于,所述的偶联剂选自硅烷偶联剂、钛酸酯偶联剂或两者复配。7.根据权利要求1或2所述的氯化聚氯乙烯...
【专利技术属性】
技术研发人员:倪锐利,崔巍,
申请(专利权)人:上海氯碱化工股份有限公司,
类型:发明
国别省市:上海,31