The invention discloses a preparation method of a coating, which boils water, butyl propionate, quartz sand powder, silicon powder and hydroxypropyl methyl cellulose after mixing, lowers the temperature to 30 C after 2 hours and adds methanol, then reduces to room temperature after holding for 30 minutes, adds alumina powder and titanium dioxide powder, and then mixes evenly. Compared with the prior art, the invention has the advantages of low cost, simple process and is suitable for popularization. At the same time, when the product of the invention is coated on the surface of the sheet metal, the sheet metal with good antistatic, waterproof and antifogging properties can be obtained.
【技术实现步骤摘要】
一种涂料的制备方法
本专利技术属于化工领域，具体涉及一种涂料的制备方法。
技术介绍
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”优质的涂料是社会所亟需的。
技术实现思路
本专利技术要解决的技术问题是提供一种涂料的制备方法，以解决现有技术存在的效果不佳的问题。为解决上述技术问题，本专利技术采用的技术方案如下：一种涂料，它包括如下重量份数的组分：其中，优选如下重量份数的组分：进一步的，优选如下重量份数的组分：上述涂料的制备方法包括如下步骤：将水、丙酸丁酯、石英砂粉末、硅粉和羟丙基甲基纤维素混合后煮沸，2小时后降温至30℃并加入甲醇，保温30分钟后再降至室温，加入氧化铝粉末和钛白粉，混合均匀后即得。上述涂料在制备防静电板材中的应用也在本专利技术的保护范围之内。上述涂料在制备防水板材中的应用也在本专利技术的保护范围之内。上述涂料在制备防雾板材中的应用也在本专利技术的保护范围之内。其中，应用方法为，将涂料涂在板材表面，即可实现防静电、防水和防防雾的效果。有益效果：与现有技术相比，本专利技术成本低廉，工艺简单，适于推广。同时，将本专利技术产品涂在板材表面，即可得到具有良好的防静电、防水和防防雾性能的板材。具体实施方式...
【技术保护点】
1.一种涂料的制备方法，其特征在于，它包括如下步骤：将水、丙酸丁酯、石英砂粉末、硅粉和羟丙基甲基纤维素混合后煮沸，2小时后降温至30℃并加入甲醇，保温30分钟后再降至室温，加入氧化铝粉末和钛白粉，混合均匀后即得。
【技术特征摘要】
1.一种涂料的制备方法，其特征在于，它包括如下步骤：将水、丙酸丁酯、石英砂粉末、硅粉和羟丙基甲基纤维素混合后煮沸，2小时后降温至30℃并加入甲醇，保温30分钟后再降至室温，加入氧化铝粉末和钛白粉，混合均匀后即...