The invention relates to a new photocatalytic paint for purifying indoor air, which is made of the following components: pigments 5_7g, polyaniline 0.04_0.06g, nano-titanium dioxide 0.5_0.7g, carbon powder 0.1_0.15g, solvent 250_300mL. The photocatalytic coating of the present invention is a clean and environmentally friendly new photocatalytic coating, which can extend the spectral response of the system to the visible region, increase the adsorption concentration and achieve high photocatalytic performance; after adding polyaniline and carbon powder, indoor polluted gases can be effectively removed, the concentration of polluted gases in the environment can be reduced, the preparation method is simple, the environment is pollution-free, safe and environmental protection.
【技术实现步骤摘要】
一种净化室内空气的新型光催化涂料及其制备方法
本专利技术属于光催化涂料领域，具体涉及一种净化室内空气的新型光催化涂料及其制备方法。
技术介绍
研究表明，光催化技术在环境污染治理方面有着良好的应用前景，光催化剂可以分散于树脂中制成光催化涂料，不但能使涂层具有优良的性能，还可以有效地降低环境中污染性气体的浓度，使有机或无机污染物在光催化作用下发生氧化还原反应，生成H2O、CO2及盐等物质，达到无害化，从而净化环境。二氧化钛(TiO2)能够捕获光子和实现电荷分离，是最常用的光催化材料。该类无机半导体光催化剂的光催化过程是通过光激发产生的电子和空穴，其分别与吸附到催化剂表面的物种发生还原和氧化反应而实现的。但是其光催化剂粉体在应用过程中面临光催化效率低和吸附量低等问题。因此，一种能够同时提高传统光催化剂的吸附量和光催化效率的高效复合材料是发展和应用光催化技术所需要的。TiO2通常有三种晶型：板钛矿、锐钛矿、金红石。板钛矿由于自然界中存在较少而较少被考虑，锐钛矿TiO2的禁带宽度为3.2eV，金红石TiO2的禁带宽度为3.0eV。因此，二氧化钛只能吸收紫外区的光线，当加入色素以后，可以吸收可见光,并且通过对文献和专利的调研并未找到该种光催化涂料，所以该种光催化涂料是一种新型的光催化涂料，对环境无任何污染。
技术实现思路
本专利技术的目的在于提供一种净化室内空气的新型光催化涂料及其制备方法。本专利技术所采用的技术方案是：一种去除室内污染气体的新型光催化涂料，由下述重量的组分制成：色素5-7g，聚苯胺0.04-0.06g，纳米二氧化钛0.5-0.7g，碳粉0.1-0.15g...
【技术保护点】
1.一种净化室内空气的新型光催化涂料，其特征在于，由下述重量的组分制成：色素5‑7g，聚苯胺0.04‑0.06g，纳米二氧化钛0.5‑0.7g，碳粉0.1‑0.15g，溶剂250‑300mL。
【技术特征摘要】
1.一种净化室内空气的新型光催化涂料，其特征在于，由下述重量的组分制成：色素5-7g，聚苯胺0.04-0.06g，纳米二氧化钛0.5-0.7g，碳粉0.1-0.15g，溶剂250-300mL。2.如权利要求1所述的净化室内空气的新型光催化涂料，其特征在于，所述色素分别为叶绿素、胡萝卜素、甜菜红色素。3.如权利要求...
【专利技术属性】
技术研发人员：邢子鹏，王平，朱琦，
申请(专利权)人：黑龙江大学，
类型：发明
国别省市：黑龙江,23