A low carbon equivalent and high expansion rate 1180 MPa cold rolled steel plate and its manufacturing method have been developed. The chemical constituents of the cold rolled steel plate are C:0.1%-0.15%, Si:0.1%-0.4%, Mn:1.5%-2.0%, Al:0.01%-0.05%, Mo:0.25-0.5%, Ti:0.08-0.16% Fe and inevitable impurities. The steel plate ensures that the steel plate achieves 1180 MPa tensile strength under low carbon equivalent condition by reasonable design of composition and manufacturing process, and the structure includes uniformly dispersed nano-sized precipitates to obtain higher precipitation strengthening effect and excellent pore expansion rate. The yield strength of the steel plate is greater than 900 MPa, the tensile strength is greater than 1180 MPa, and the hole enlargement ratio is more than 35%.
【技术实现步骤摘要】
一种低碳当量高扩孔率1180MPa级冷轧钢板及其制造方法
本专利技术涉及一种冷轧钢板及其制造方法,尤其涉及一种低碳当量高扩孔率1180MPa级冷轧钢板及其制造方法,该钢板具有900MPa以上的屈服强度,1180MPa以上的抗拉强度,优良的扩孔率。
技术介绍
随着全球能源危机和环境问题的加剧,节能和安全成为了汽车制造业的主要发展方向。降低车重是节能和减少排放措施之一。高强度双相钢具有良好的机械性能和使用性能,适于结构件的制造。随着减重节能的趋势不断发展,未来双相钢的中心强度级别预计会上移,1180DP的需求将增加,但前提是要求1180DP具有和980DP相当的成型性能和焊接性能。本专利技术介绍了一种低碳当量高扩孔率1180MPa级冷轧钢板及其制造方法,符合双相钢的发展前景,有很好的发展前景。现有高扩孔冷轧超高强钢设计与本专利技术有较大区别。传统的冷轧钢板为了获得高扩孔率,工艺路线是尽量保证组织均一,一般路线为使基体获得高比例的贝氏体组织(一般为贝氏体含量70%以上的复相钢),从而减小组织的强度差别,提高扩孔率。这样的技术路线有固有缺点:均一的贝氏体组织可以保证较高扩孔率,但难以保证超过1180MPa的强度;而且含高比例贝氏体组织基体的延伸率不高,材料的加工性能下降。另外一些其他获得高扩孔率冷轧高强钢的专利也与本专利技术有明显区别:如:中国专利申请公开号CN106164313公开了一种伸长率、扩孔率、耐延迟开裂性能优异的超高强度冷轧钢板及其制造方法。其C:0.13-0.25%,Si:1.2-2.2%,Mn:2.0-3.2%,P:0.08%以下,S:0.005% ...
【技术保护点】
1.一种低碳当量高扩孔率1180MPa级冷轧钢板,其化学成分质量百分比为:C:0.1%~0.15%,Si:0.1%~0.4%,Mn:1.5%~2.0%,Al:0.01%~0.05%,Mo:0.25~0.5%,Ti:0.08~0.16%,余量为Fe和其他不可避免杂质;且,满足:1.45≥3×[C]+0.4×[Si]+0.25×[Mn]2≥1.1,[Mo]≥3×[Ti]。
【技术特征摘要】
1.一种低碳当量高扩孔率1180MPa级冷轧钢板,其化学成分质量百分比为:C:0.1%~0.15%,Si:0.1%~0.4%,Mn:1.5%~2.0%,Al:0.01%~0.05%,Mo:0.25~0.5%,Ti:0.08~0.16%,余量为Fe和其他不可避免杂质;且,满足:1.45≥3×[C]+0.4×[Si]+0.25×[Mn]2≥1.1,[Mo]≥3×[Ti]。2.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述C含量为0.11%~0.14%。3.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述Si含量为0.2%~0.3%。4.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述Mn含量为1.6%~1.9%。5.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述Al含量为0.015~0.045%。6.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述Mo含量为0.3%~0.45%。7.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述Ti含量为0.1%~0.14%。8.如权利要求1所述的低碳当量高扩孔率1180MPa级冷轧钢板,其特征在于:所述碳当量Pcm...