A method for synthesizing single-phase LaFeO3 in molten salt system belongs to the field of material preparation. Firstly, a certain amount of NaCl, Na2CO3, Fe (NO3) 3.9H_2O and La (NO3) 3.nH_2O were weighed and mixed evenly; after fully drying, they were ground and mixed, and then transferred to the muffle furnace for roasting. At the rate of 5 C/min, they were heated from room temperature to 700 C, kept for 4 h, and cooled naturally to room temperature. After dissolution, filtration, washing and drying, LaFeO_3 catalyst was obtained. The method and process described in the invention are simple and convenient for industrial production.
【技术实现步骤摘要】
一种熔融盐体系合成单相LaFeO3的方法
本专利技术涉及一种新型熔融盐体系合成单相LaFeO3的方法,从而减少能耗、提高稳定性的方法,属于材料制备领域。
技术介绍
挥发性有机物(VOCs)是目前主要的大气污染物之一。催化氧化法具有高效节能、去除率高、适用范围广等特点,是消除低浓度VOCs的有效方法之一。高效催化剂的研发成为该技术的核心。目前用于催化氧化VOCs的催化剂主要有过渡金属氧化物催化剂、复合型氧化物催化剂和负载贵金属催化剂,成本低廉的钙钛矿型复合氧化物如LaFeO3钙钛矿型复合氧化物具有优良的热稳定性和耐化学腐蚀性,适合催化燃烧负载、较高浓度的有毒VOCs。在本专利技术中我们采用新型熔融盐体系合成了单相的LaFeO3钙钛矿型复合氧化物。
技术实现思路
本专利技术的目的在于提供一种新型熔融盐体系合成单相LaFeO3的方法。为实现上述目的,本专利技术步骤包括如下:(1)称取一定量的NaCl、Na2CO3、Fe(NO3)3.9H2O和La(NO3)3.nH2O,混合均匀;(2)将步骤(1)的混合药品放在鼓风式烘箱中充分烘干,再进行研磨混合均匀;(3)将步骤(2)所得粉末转移至马弗炉内,以5℃/min的速率从室温升至700℃,保温4h,自然冷却至室温,经溶解、抽滤、洗涤、干燥后得到LaFeO3催化剂。步骤(1)选用的熔融盐体系中NaCl、Na2CO3的质量比为6.46:9.47,Fe(NO3)3.9H2O和La(NO3)3.nH2O的质量比为1.21:0.97。,进一步优选NaCl与Fe(NO3)3.9H2O的质量比为6.46:(1.0-1.4),优选6.46 ...
【技术保护点】
1.一种熔融盐体系合成单相LaFeO3的方法,其特征在于,包括以下步骤:(1)称取一定量的NaCl、Na2CO3、Fe(NO3)3·9H2O和La(NO3)3·nH2O,混合均匀;(2)将步骤(1)的混合药品放在鼓风式烘箱中充分烘干,再进行研磨混合均匀;(3)将步骤(2)所得粉末转移至马弗炉内,以5℃/min的速率从室温升至700℃,保温4h,自然冷却至室温,经溶解、抽滤、洗涤、干燥后得到LaFeO3催化剂;步骤(1)选用的熔融盐体系中NaCl、Na2CO3的质量比为6.46:9.47,Fe(NO3)3·9H2O和La(NO3)3·nH2O的质量比为1.21:0.97。
【技术特征摘要】
1.一种熔融盐体系合成单相LaFeO3的方法,其特征在于,包括以下步骤:(1)称取一定量的NaCl、Na2CO3、Fe(NO3)3·9H2O和La(NO3)3·nH2O,混合均匀;(2)将步骤(1)的混合药品放在鼓风式烘箱中充分烘干,再进行研磨混合均匀;(3)将步骤(2)所得粉末转移至马弗炉内,以5℃/min的速率从室温升至700℃,保温4h,自然冷却至室温,经溶解、抽滤、洗涤、干燥后得到LaFeO3催化剂;步骤(1)选用的熔融盐体...