The invention belongs to the field of synthesis of electronic materials and adhesives, and relates to a synthesis process of PTC functional waterborne adhesives. The present invention is a reactive synthetic conductive binder. The conductive component is uniformly modified on graphene oxide by in-situ polymerization, and then reduced by KI. At the same time, the product I2 is absorbed by polyaniline molecule to increase the conductivity synergistically. The invention synthesizes PTC functional waterborne adhesive for connecting element pins and circuit boards and performing PTC current limiting protection function.
【技术实现步骤摘要】
一种PTC功能水性胶的合成工艺
本专利技术属于电子材料和胶粘剂合成领域,涉及一种PTC功能水性胶的合成工艺。
技术介绍
正温度系数(PTC)材料的电阻率随温度的升高而增大,高分子与导电填料共混可制得的复合材料(PPTC)具有较低的室温电阻率,随温度升高电阻率增加并在某个温度点电阻急剧升高,在大电流状态下电阻急剧增加实现电路关断,并可在故障排除后自行恢复低阻状态。目前,在电路保护方案中,SMD贴片PPTC元件需要挤占线路板上的宝贵面积,另外分立元件的焊接、线路设计等因素也会增加整体器件的制造成本。另外,SMD元件制造过程中大量压合、粘接以及焊接的界面,冗长工序都会对元件良率以及最终焊接元件功能失效产生影响。
技术实现思路
针对现有技术缺陷,本专利技术的目的在于提供一种PTC功能水性胶的合成工艺,其特征在于,包括如下步骤:(1)将苯胺单体和氧化石墨加入去离子水中,超声分散得到紫褐色溶胶;(2)配制丙烯酸乳液,成分及质量比为:去离子水100份丙烯酸丁酯40-50份甲基丙烯酸10-15份丙烯酸5-8份过硫酸钾10-20份十二烷基硫酸钠0.5-1份(3)将步骤(1)得到的溶胶加入步骤(2)的丙烯酸乳液中,室温搅拌反应2-5小时,加入碘化钾,继续反应1-2小时;(4)加入固化剂和其他助剂,搅拌稠化得到水性胶。所述氧化石墨的加入量为在步骤(3)混合乳液浓度0.2~1.5gL-1;超声分散时间为1~2h。苯胺单体在在步骤(3)混合乳液浓度中的浓度为0.1~0.5molL-1。所述碘化钾加入后浓度为10~20g/L,。固化剂为胺类固化剂,包括乙二胺、间苯二胺、对苯二胺、间苯二甲 ...
【技术保护点】
1.一种PTC功能水性胶的合成工艺,其特征在于,包括如下步骤:(1)将苯胺单体和氧化石墨加入去离子水中,超声分散得到紫褐色溶胶;(2)配制丙烯酸乳液,成分及质量比为:去离子水 100份丙烯酸丁酯 40‑50份甲基丙烯酸 10‑15份丙烯酸 5‑8份过硫酸钾 10‑20份十二烷基硫酸钠 0.5‑1份(3)将步骤(1)得到的溶胶加入步骤(2)的丙烯酸乳液中,室温搅拌反应2‑5小时,加入碘化钾,继续反应1‑2小时;(4)加入固化剂和其他助剂,搅拌稠化得到水性胶。
【技术特征摘要】
1.一种PTC功能水性胶的合成工艺,其特征在于,包括如下步骤:(1)将苯胺单体和氧化石墨加入去离子水中,超声分散得到紫褐色溶胶;(2)配制丙烯酸乳液,成分及质量比为:去离子水100份丙烯酸丁酯40-50份甲基丙烯酸10-15份丙烯酸5-8份过硫酸钾10-20份十二烷基硫酸钠0.5-1份(3)将步骤(1)得到的溶胶加入步骤(2)的丙烯酸乳液中,室温搅拌反应2-5小时,加入碘化钾,继续反应1-2小时;(4)加入固化剂和其他助剂,搅拌稠化得到水性胶。2.根据权利要求1所述一种PTC功能水性胶的合成工艺,其特征在于,所述氧化石墨的加入量为在步骤(3)混合乳液浓度0.2~1.5gL-1;超声分散时间为1~2h。苯胺单体在在步骤(3...
【专利技术属性】
技术研发人员:汪元元,
申请(专利权)人:合肥萃励新材料科技有限公司,
类型:发明
国别省市:安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。