The aim of the present invention is to provide a preparation method for synthesizing tin hydroxide strontium nanorods by solid-phase chemical method at room temperature. The method uses cheap raw materials: different solid strontium salts, tin chloride and sodium hydroxide as reactants, and synthesizes tin hydroxide strontium nanorods by direct chemical reaction of solid-phase and solid-phase at room temperature through simple operation process. The preparation method of Sn-Sr hydroxide nanorods provided by the invention has the characteristics of low cost, simple operation, short time and easy to realize mass production, which makes the invention have extremely broad application prospects.
【技术实现步骤摘要】
一种室温固相化学法合成氢氧锡锶纳米棒的方法
本专利技术涉及一种室温固相化学法合成氢氧锡锶纳米棒的方法。
技术介绍
双金属氢氧化物(氢氧锡钴、氢氧锡锌、氢氧锡锶等)因呈现出较好的导电性、光学性质和耐酸碱性而逐渐引起了人们的广泛关注,被广泛应用于催化、锂离子电池以及超级电容器等领域。氢氧锡锶作为双金属氢氧化物中的代表之一,将其制备的纳米材料,特别是一维纳米材料,具有强氧化能力和矿化能力,也具有好的光催化活性。目前,液相共沉淀法是一维氢氧锡锶纳米棒的主要合成方法。但是,由于其合成过程需要使用极高浓度的强碱溶液(如1.2mol/L氢氧化钠),这不仅增加了反应过程中的实验安全隐患,而且高浓度强碱的后处理过程也较为繁琐。因此,选择一种绿色、简单的制备方法,制备氢氧锡锶纳米棒具有十分重要的意义。室温固相化学合成法不使用溶剂,具有高选择性、高产率、工艺过程简单、低能耗等优点,已经成为合成无机纳米材料的一种重要方法。
技术实现思路
本专利技术的目的在于提供一种室温固相化学法合成氢氧锡锶纳米棒的制备方法,该方法通过使用廉价的原料,采用简单的操作过程,经室温固相化学反应合成出氢氧锡锶纳米棒。本专利技术用氯化锡、氢氧化钠和不同的固体锶盐作为反应物,在室温下通过固相化学反应合成氢氧锡锶纳米棒。本专利技术所述的锶盐为硝酸锶、乙酸锶和氯化锶中的一种。与现有技术相比,本专利技术具有以下优点:以固相化学反应为基础,采用廉价易得的原料,在室温条件下通过简单的固相化学反应,制得氢氧锡锶纳米棒。制备方法具有操作简单,成本低,时间短,产品产率高,环境友好,易于实现大批量生产等特点,使得本专利技术具有极 ...
【技术保护点】
1.一种室温固相化学反应制备氢氧锡锶纳米棒的方法,其包括以下步骤 :将氯化锡、氢氧化钠与不同的固体锶盐按一定比例进行混合,在室温条件下进行固相化学反应,将反应后的混合物用去离子水洗涤后得到最终的氢氧锡锶纳米棒。
【技术特征摘要】
1.一种室温固相化学反应制备氢氧锡锶纳米棒的方法,其包括以下步骤:将氯化锡、氢氧化钠与不同的固体锶盐按一定比例进行混合,在室温条件下进行固相化学反应,将反应后的混合物用去离子水洗涤后得到最终的氢氧锡锶纳米棒。2.按照权利要求1所述的一种室温固相化学法合成氢氧锡锶纳米棒的方法,其特征在于:所使...