The invention relates to the field of ceramic materials, in particular to a preparation method of high toughness ceramics, which includes the following steps: the first step is to weigh the following raw materials: alumina 88%95%, silicon nitride 5%12%; the second step is to mix raw materials by wet method, and organic solvents are used in wet mixing; Step, add ball mill for ball milling; Step 4, forming, dewatering slurry powder with filter press to provide blanks to the forming process; Step 5, sintering. The preparation method of the high toughness ceramics of the invention is simple and easy to operate, and the prepared ceramics have high toughness and low cost.
【技术实现步骤摘要】
高韧性陶瓷的制备方法
本专利技术涉及陶瓷材料领域,具体而言,涉及一种高韧性陶瓷的制备方法。
技术介绍
陶瓷材料具有耐高温、耐磨损、耐腐蚀及重量轻等优良性能,但是陶瓷材料同时也具有致命的缺点--脆性,在室温下承载时几乎不能产生塑性变形,这一缺点使得陶瓷材料的应用受到很大限制。提高陶瓷材料的韧性是近年来研究的一个重点问题。韧性陶瓷具有强度大、硬度高、耐高温、耐化学腐蚀等优越性能,在工业上有着重要的用途。高韧性陶瓷可以代替一些金属用品,比如机车外壳、路灯等,以减少金属的腐蚀,提高产品的使用寿命,减少对环境的污染。
技术实现思路
本专利技术的主要目的在于针对上述问题提供一种高韧性陶瓷的制备方法。为了实现上述目的,本专利技术的高韧性陶瓷的制备方法,包括以下步骤:第一步,称取以下重量份的原料:氧化铝88%-95%,氮化硅5%-12%;第二步,将原料采用湿法混合,湿法混合中采用有机溶剂;第三步,加入球磨机进行球磨;第四步,成型,用压滤机将料浆状的粉脱水后成坯料供给成型工序;第五步,烧结。进一步的,原料的粒径为3-6μm,纯度为98%以上。进一步的,球采用陶瓷球,内衬也采用陶瓷。进一步的,烧结温度为1200°-1250°,保温时间为1.5-2小时。本专利技术具有以下有益效果:本专利技术的高韧性陶瓷的制备方法步骤简单易操作,制备出来的陶瓷韧性高,成本低。具体实施方式本专利技术的高韧性陶瓷的制备方法,包括以下步骤:第一步,称取以下重量份的原料:氧化铝92%,氮化硅8%,原料的粒径为3-6μm,纯度为98%以上;第二步,将原料采用湿法混合,湿法混合中采用有机溶剂;第三步,加入球磨机 ...
【技术保护点】
1.一种高韧性陶瓷的制备方法,其特征在于,包括以下步骤:第一步,称取以下重量份的原料:氧化铝88%‑95%,氮化硅5%‑12%;第二步,将原料采用湿法混合,湿法混合中采用有机溶剂;第三步,加入球磨机进行球磨;第四步,成型,用压滤机将料浆状的粉脱水后成坯料供给成型工序;第五步,烧结。
【技术特征摘要】
1.一种高韧性陶瓷的制备方法,其特征在于,包括以下步骤:第一步,称取以下重量份的原料:氧化铝88%-95%,氮化硅5%-12%;第二步,将原料采用湿法混合,湿法混合中采用有机溶剂;第三步,加入球磨机进行球磨;第四步,成型,用压滤机将料浆状的粉脱水后成坯料供给成型工序;第五步,烧结。2.根据权利...
【专利技术属性】