The invention discloses a gas phase rust inhibitor for carbon steel, which is prepared from the following weight components: benzotriazole 10_13, potassium iodide 10_13, sodium tungstate 7_9, Urotropine 11_13, urea 20_28, sodium dodecylbenzenesulfonate 10_20, water 0_0. If the above materials are mixed and stirred evenly, the gas phase rust inhibitor of carbon steel can be made. The antirust agent of the invention has the advantages of simple formulation, convenient preparation, non-toxicity, harmlessness and environmental protection. The slow-release rate of the antirust agent to carbon steel can reach 91.07%. It has excellent antirust performance and can be used for preparing antirust paper or antirust film.
【技术实现步骤摘要】
一种碳钢气相防锈剂
本专利技术涉及金属防锈
，更具体地说是涉及一种碳钢气相防锈剂。
技术介绍
碳钢是含碳量在0.0218％～2.11％的铁碳合金。碳钢可以用于制造螺栓、螺母以及其它结构比较复杂的机械零件。然而碳钢在储存、运输过程中会发生表面锈蚀，尤其是一些带有细小内腔的结构更容易发生锈蚀。在我国防锈领域，常用的是防锈油、气相防锈纸、气相防锈薄膜。但是，防锈油不易完整涂抹在金属零件的细小结构部分，适用范围有限。气相防锈纸、气相防锈薄膜的气相防锈剂中多含有亚硝酸盐，不利于环境保护，因此，亚硝酸盐类缓蚀剂已被淘汰。
技术实现思路
本专利技术要解决的技术问题是提供一种针对碳钢防锈的高效、环保的气相防锈剂。为此，本专利技术的技术方案如下：一种碳钢气相防锈剂，由下述重量份的原料制备而成：在本专利技术的一个实施例中，各原料的配比为：在本专利技术的另一实施例中，各原料的配比为：将上述物料混合，搅拌均匀，即可制成碳钢气相防锈剂。本专利技术具有以下有益效果：本专利技术的防锈剂配方简单、制备方便且无毒无害、绿色环保，对碳钢的缓释率可以达到91.07％，具有优良的防锈性能，可以用于制备防锈纸或防锈薄膜。具体实施方式下面结合实施例，对本专利技术的防锈剂作进一步详细描述。实施例1一种碳钢气相防锈剂，由以下重量份的组分制备而成：将上述物料混合，搅拌均匀，即可制成碳钢气相防锈剂。该气相防锈剂对碳钢的缓释效率为90.89％。实施例2一种碳钢气相防锈剂，由以下重量份的组分制备而成：：将上述物料混合，搅拌均匀，即可制成碳钢气相防锈剂。该气相防锈剂对碳钢的缓释效率为91.07％。缓蚀剂的评价采...
【技术保护点】
1.一种碳钢气相防锈剂，其特征在于，由下述重量份的原料制备而成：
【技术特征摘要】
1.一种碳钢气相防锈剂，其特征在于，由下述重量份的原料制备而成：2.根据权利要求1所述的碳钢气相防锈...