The invention relates to a preparation method of emulsion type cationic dry strength agent for papermaking and its application, including: (1) adding cationic monomer and acrylate monomer into a reactor, heating up to 80 pH 85, and polymerizing with azo two isobutadiene to form a surface active polymer, adding water to dissolve and adjusting the 5 to 6; (2) The acrylamide monomer, acrylate monomer, cross-linking monomer, cationic monomer and emulsifier were premixed as A, and the oxidant and deionized water were mixed into the dropping liquid B. (3) A and B drops were added to the reactor, the reaction temperature was 80? 85 degrees C, after the reaction was finished, the temperature was lowered and the deionized water was added. The reaction product of the invention can effectively avoid the phenomenon of local explosion and gelation, and form a stable emulsion system under the emulsification function of the polymer system with surface active, thereby gradually synthesizing the emulsion type cationic dry strength agent with moderate molecular weight, degree of branching and viscosity.
【技术实现步骤摘要】
一种造纸用乳液型阳离子干强剂的制备方法及其应用
本专利技术属于纸张增强剂
,具体涉及一种造纸用乳液型阳离子干强剂的制备方法及其应用。
技术介绍
干强剂是造纸工业中增强纸张强度的一类重要化学品,通常用于补偿添加填料或低等级的纤维(如再生纤维)所引起的纸强度的下降。许多水溶性的,与纤维能形成氢键的高聚物都可以成为干强剂。常用的干强剂有天然聚合物如淀粉及其改性物(阳离子淀粉、阴离子淀粉、交联淀粉)、合成聚合物如聚丙烯酰胺、聚乙烯醇等一类其他水溶性天然产物类干强剂(如瓜而胶及其衍生物等)。在大多数情况下,仅加热质量分数0.1-0.75%的该类物质就可达到有效的干强效果。近年来,我国废纸资源利用率逐年上升,并且发展潜力巨大。但废纸的利用率的提高意味着废纸循环使用次数的增加,会造成纸强度指标的大幅下降,所以需要添加干强剂来增加纸张强度。随着消费市场对纸和纸板需求量的不断的上升,拉动了干强剂需求量的迅猛增长。纸张干强剂已经被广泛用于各类纸和纸张的生产过程中,用以显著增加纸和纸板的干强度,降低优质原材料消耗、降低生产成本;或者提高产品档次,以满足用户不断提出的越来越高的质量要求。目前应用效果最好的干强剂是聚丙烯酰胺及其共聚物,包括阴离子型聚丙烯酰胺、阳离子型聚丙烯酰胺和两性聚丙烯酰胺。其中,两性聚丙烯酰胺表现出最好的应用效果。聚丙烯酰胺从结构上看还分直链型和支链型。支化度高的聚丙烯酰胺具有更好的应用效果。目前合成高性能干强剂的主流和趋势是合成分子量和粘度适中的支链型聚合物。这种干强剂可以在不添加硫酸铝的情况下起到很好的纸张干增强作用。常采用加入交联剂的方法来获得支链 ...
【技术保护点】
1.一种造纸用乳液型阳离子干强剂的制备方法,包括以下步骤:(1)将阳离子单体和丙烯酸酯单体混合作为底料,升温至80‑85℃,以偶氮二异丁腈引发聚合,制得具有表面活性的高分子聚合物,加水溶解并用调节pH为5‑6;(2)将丙烯酰胺单体、丙烯酸酯单体、交联单体、阳离子单体以及乳化剂配成预乳液,作为滴加液A;将氧化剂和去离子水混合配成引发体系,作为滴加液B;(3)将滴加液A、B同时匀速滴加到步骤(1)的物料中,反应温度为80‑85℃;反应完毕后,降温并补充去离子水,即得乳液型阳离子干强剂。
【技术特征摘要】
1.一种造纸用乳液型阳离子干强剂的制备方法,包括以下步骤:(1)将阳离子单体和丙烯酸酯单体混合作为底料,升温至80-85℃,以偶氮二异丁腈引发聚合,制得具有表面活性的高分子聚合物,加水溶解并用调节pH为5-6;(2)将丙烯酰胺单体、丙烯酸酯单体、交联单体、阳离子单体以及乳化剂配成预乳液,作为滴加液A;将氧化剂和去离子水混合配成引发体系,作为滴加液B;(3)将滴加液A、B同时匀速滴加到步骤(1)的物料中,反应温度为80-85℃;反应完毕后,降温并补充去离子水,即得乳液型阳离子干强剂。2.根据权利要求1所述的乳液型阳离子干强剂的制备方法,其特征在于,步骤(1)中阳离子单体占底料总质量的50-60%,丙烯酸酯单体占底料总质量的40-50%;优选的,引发剂偶氮二异丁腈的添加量为底料总重量的0.1-0.2%。3.根据权利要求1所述的乳液型阳离子干强剂的制备方法,其特征在于,步骤(2)滴加液A中丙烯酰胺单体占丙烯酰胺单体和丙烯酸酯单体总质量的43-54%,丙烯酸酯单体占丙烯酰胺单体和丙烯酸酯单体总质量的46-67%;交联单体的添加量为丙烯酰胺单体和丙烯酸酯单体总质量的2.5-3.6%,阳离子单体的添加量为丙烯酰胺单体和丙烯酸酯单体总质量的14.5-16.5%,乳化剂的添加量为丙烯酰胺单体和丙烯酸酯单体总质量的0.8-1.2%;滴加液B中氧化剂的使用量为丙烯酰胺单体和丙烯酸酯单体总质量的0.2~0.5%。4.根据权利要求1所述的乳液型阳离子干强剂的制备方法,其特征在于,步骤(3)中底料的总质量:滴加液A中丙烯酰胺单体和丙烯酸酯单体总质量比为1.1:10-1.5:10。5.根据权利要求1所述的乳液型阳离子干强剂的制备方法,其特征在于,步骤(1)-(2)中所述丙烯酸酯单体选自...
【专利技术属性】
技术研发人员:谢鹏,白永亮,
申请(专利权)人:山东金元化工股份有限公司,
类型:发明
国别省市:山东,37