The invention discloses a preparation method of wallpaper base paper, which comprises the following steps: (1) mixing coniferous wood mechanical pulp with hardwood mechanical pulp, adding bleached chemical coniferous pulp and bleached chemical hardwood, stirring and mixing to obtain mixed pulp; (2) mixing mixed pulp with biogas slurry and fermenting at constant temperature to obtain activated wood pulp; (3) Protein fibers and protease were mixed; (4) glass fibers and hydrochloric acid were mixed; (5) graphite oxide and talc powder were mixed, and nano-silica was added, and the additives were mixed by ball milling; (6) the green material was obtained, and the green material was moved into the machine to make, dry and get the wallpaper base paper. The water resistance of the invention is improved. Secondly, the modified protein fiber and glass fiber can be adsorbed on the cellulose of the pulp after being added to the wood pulp, so as to improve the mechanical properties and stability of the small cellulose molecules in the pulp, thereby improving the mechanical properties and stability of the product.
【技术实现步骤摘要】
一种壁纸原纸的制备方法
本专利技术涉及一种壁纸原纸的制备方法。
技术介绍
随着人们生活水平的提高和环保意识的增强,用于家装的传统化石涂料已逐步被环保型壁纸所取代。为满足墙体装饰要求,作为壁纸基层的原纸,其要求具有较好的抗张强度、尺寸稳定性、不透明度、疏水、挺度和松厚度等。壁纸原纸要求稳定性好,最主要的指标就是要控制好原纸的伸缩率,一般要求原纸横向伸缩率不能超过1.5%。影响壁纸原纸伸性能的因素很多:(1)不同浆料的选择:同一种制浆方法,草浆伸缩性最大,针叶木浆次之,阔叶木浆最小;而同一材种,硫酸盐浆伸缩性最大,亚硫酸盐浆次之,机械浆最小。(2)打浆度:生产实践证明:打浆度愈高,纤维的润胀、水化、细纤维化程度愈高,抄成的纸张伸缩率也愈大。降低打浆度、控制湿重,使之不影响纸张匀度,即需要尽量避免浆料纤维的分丝帚化,适当增加纤维切断,降低湿重。(3)抄造:正常生产过程中纸页的横向伸缩率比纵向伸缩率要大,其主要原因有两点:a.纤维从流浆箱上网后在纸张纵向排列的数量比横向排列的多,所以纤维的纵向变形小而横向变形大;b.当纸页离开网部时,纸幅前进要保持一定的张力,阻碍了纸幅的纵向收缩,而横向收缩则比较大,所以纸张的横向变形也大。解决壁纸原纸伸缩过大的问题可先从原料着手,合理配比。漂白化学热磨机械浆(BCTMP)具有生产成本低,成形好,不透明度和松厚度高,纸页挺度较高及透气度较低等优点,可作为生产壁纸原纸的较好原料之一。BCTMP纤维虽挺度较高,但其纤维所抄造纸页的抗张强度和抗水性较差。适当添加漂白硫酸盐木浆可部分改善上述不足,但生产的壁纸原纸物理强度仍然较差,且所产生 ...
【技术保护点】
1.一种壁纸原纸的制备方法,其特征在于,包括如下步骤:(1)将针叶木机械浆与阔叶木机械浆按质量比5:1混合,并加入针叶木机械浆质量0.1倍的漂白化学针叶木浆和针叶木机械浆质量0.11倍的漂白化学阔叶木浆,搅拌混合后,得混合浆料;(2)将混合浆料与沼液按质量比9:1混合,恒温发酵,得活化木浆;(3)将蛋白质纤维与蛋白酶按质量比19:1混合,常温酶解,得降解蛋白质纤维;(4)将玻璃纤维与盐酸按质量比1:2混合,搅拌反应后,过滤,得酸化玻璃纤维;(5)将氧化石墨与滑石粉按质量比2:1混合,并加入氧化石墨质量0.5倍的纳米二氧化硅,球磨混合得添加剂;(6)按重量份数计,依次称取69份活化木浆,9份降解蛋白质纤维,9份酸化玻璃纤维,5份生物质焦油,1份聚酰胺环氧氯丙烷树脂,3份硫酸铝,2份表面活性剂和7份添加剂,将活化木浆和降解蛋白质纤维加入搅拌机中搅拌混合后,再依次向搅拌机中加入酸化玻璃纤维,生物质焦油,聚酰胺环氧氯丙烷树脂,硫酸铝,表面活性剂和添加剂,搅拌混合后,得混合物,将混合物加入打浆机中打浆,得坯料,将坯料移入抄造机中抄造,烘干,得壁纸原纸。
【技术特征摘要】
1.一种壁纸原纸的制备方法,其特征在于,包括如下步骤:(1)将针叶木机械浆与阔叶木机械浆按质量比5:1混合,并加入针叶木机械浆质量0.1倍的漂白化学针叶木浆和针叶木机械浆质量0.11倍的漂白化学阔叶木浆,搅拌混合后,得混合浆料;(2)将混合浆料与沼液按质量比9:1混合,恒温发酵,得活化木浆;(3)将蛋白质纤维与蛋白酶按质量比19:1混合,常温酶解,得降解蛋白质纤维;(4)将玻璃纤维与盐酸按质量比1:2混合,搅拌反应后,过滤,得酸化玻璃纤维;(5)将氧化石墨与滑石粉按质量比2...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。