The invention provides a preparation method of high-temperature nanobentonite. The raw ore bentonite is first crushed and homogenized, then sifted to obtain the raw ore, and then the raw ore is added with a surface modifier of 0.5_5%, a nano-chemical agent of 7_10% and an activator of 1.5_3%. After mixing, the temperature is raised to 200_300 degrees Celsius. After natural cooling to room temperature, the sodium bentonite was obtained by aging and drying. The invention has good dispersibility in water medium and high colloid price; its colloid suspension has good thixotropy, viscosity, lubricity, high pH value; good thermal stability; high plasticity and strong cohesion; high hot-wet tensile strength and dry compressive strength.
【技术实现步骤摘要】
一种高温纳基膨润土制备方法
本专利技术涉及膨润土制备领域,具体是一种高温纳基膨润土制备方法。
技术介绍
膨润土矿是一种多种用途的矿产,其质量和应用领域主要取决于其中蒙脱石含量和属性类型及其晶体化学特性。因而,其开发利用必须因矿而异,因作用而异。如生产活性白土,钙基转钠基,供石油钻探用的钻井注浆,代替淀粉用于纺纱、印染的浆料,建材上用内外墙涂料,制备有机膨润土,用膨润土合成4A沸石、生产白炭黑等等。钠基膨润土是根据蒙脱石层间可交换阳离子种类、含量来划分:碱性系数大于或等于1的为钠基膨润土,小于1的为钙基膨润土。目前技术常温下制备的纳基膨润土各方面都不如天然钠基膨润土。天然钠基膨润土的膨胀力比人工钠基膨润土大;天然钠基膨润土比人工钠基膨润土c轴有序度高,晶粒较细,分散性强。
技术实现思路
本专利技术为了解决现有技术的问题,提供了一种高温纳基膨润土制备方法,在水介质中分散性好,胶质价高;它的胶体悬浮液触变性、粘度、润滑性好,pH值高;热稳定性好;有较高的可塑性和较强的粘结性;热湿拉强度和干压强度高。本专利技术包括以下步骤:1)将原矿膨润土进行粉碎均化处理后,粒径筛分,得到原矿土;2)在原矿土加入原矿土质量0.5-5%的表面修饰剂、7-10%的纳化剂以及1.5-3%的活化剂,混合后升温到200-300摄氏度;所述的活化剂为锌类化合物;3)自然冷却至室温,进行陈化处理、干燥处理,得到钠基膨润土。进一步改进,所述的纳化剂为碳酸钠、硅酸钠、氟化钠、草酸钠、醋酸钠、磷酸类钠盐、聚丙烯酸钠、氢氧化钠、氯化钠、硫代硫酸钠和纤维素钠中的一种或多种。进一步改进,所述的锌类化合物为氯化 ...
【技术保护点】
1.一种高温纳基膨润土制备方法,其特征在于包括以下步骤:1)将原矿膨润土进行粉碎均化处理后,粒径筛分,得到原矿土;2)在原矿土加入原矿土质量0.5‑5%的表面修饰剂、7‑10%的纳化剂以及1.5‑3%的活化剂,混合后升温到200‑300摄氏度;所述的活化剂为锌类化合物;3)自然冷却至室温,进行陈化处理、干燥处理,得到钠基膨润土。
【技术特征摘要】
1.一种高温纳基膨润土制备方法,其特征在于包括以下步骤:1)将原矿膨润土进行粉碎均化处理后,粒径筛分,得到原矿土;2)在原矿土加入原矿土质量0.5-5%的表面修饰剂、7-10%的纳化剂以及1.5-3%的活化剂,混合后升温到200-300摄氏度;所述的活化剂为锌类化合物;3)自然冷却至室温,进行陈化处理、干燥...