The invention discloses a kind of anti bending cable outer sheath material for mine. According to the weight, it consists of the following components: 45 methyl vinyl silicone rubber, 60 parts, 20 styrene butadiene resin, 18 Magnesium Oxide 28 copies, 8 calcined clay 15, 12 calcium carbonate, 5 calcium carbonate, 15 portion of calcium carbonate, 20 stabilizers 3. Parts, barium stearate 6, 12, flame retardant 2, 5 and synergist 4, 7. The outer sheath material of the invention is scientific and reasonable, with good heat and oxygen aging, high breaking elongation, long service life, high impact resistance and bending resistance, and can effectively improve the electrical, mechanical and flame retardant properties of the flame retardant cable material, and is suitable for mine engineering.
【技术实现步骤摘要】
一种矿井用抗弯折电缆外护套材料
本专利技术涉及到电缆生产制造
,尤其是一种矿井用抗弯折电缆外护套材料。
技术介绍
随着我国市场经济的快速发展,煤炭工业作为当今世界主要能源的基础工艺之一获得迅速发展,对矿井的安全更是引起人们的重视,由于井下工作环境恶劣,各种事故的发生严重威胁着矿井的安全和矿工的生命,与之配套的电缆阻燃性能同样引人关注,阻燃电缆为当电缆因故自身着火或是外火源引燃着火时,在着火熄灭后电缆不再继续燃烧,或燃烧时间很短,如何制备一种高效阻燃的电缆护套成为目前需要解决的技术问题。
技术实现思路
本专利技术的目的在于提供一种矿井用抗弯折电缆外护套材料,配比科学合理,耐热氧老化性能好、断裂伸长率高,使用寿命长具有较高的抗冲击性能、抗弯折性能,能有效的提高了阻燃电缆料电气、机械、阻燃性能,适用于矿井工程。为实现上述目的,本专利技术提供如下技术方案:一种矿井用抗弯折电缆外护套材料,按照重量份由以下成分组成:甲基乙烯基硅橡胶45-60份、丁苯树脂20-30份、氧化镁18-28份、煅烧陶土8-15份、气相法白炭黑8-12份、碳酸钙5-15份、稳定剂3-7份、乙醇10-15份、硬脂酸钡6-12份、阻燃剂2-5份和复合增效剂4-7份。进一步的,上述一种矿井用抗弯折电缆外护套材料,按照重量份由以下成分组成:甲基乙烯基硅橡胶55-60份、丁苯树脂26-30份、氧化镁24-28份、煅烧陶土12-15份、气相法白炭黑10-12份、碳酸钙13-15份、稳定剂5-7份、乙醇12-15份、硬脂酸钡9-12份、阻燃剂4-5份和复合增效剂6-7份。进一步的,上述一种矿井用抗弯折电缆 ...
【技术保护点】
一种矿井用抗弯折电缆外护套材料,其特征在于,按照重量份由以下成分组成:甲基乙烯基硅橡胶45‑60份、丁苯树脂20‑30份、氧化镁18‑28份、煅烧陶土8‑15份、气相法白炭黑8‑12份、碳酸钙5‑15份、稳定剂3‑7份、乙醇10‑15份、硬脂酸钡6‑12份、阻燃剂2‑5份和复合增效剂4‑7份。
【技术特征摘要】
1.一种矿井用抗弯折电缆外护套材料,其特征在于,按照重量份由以下成分组成:甲基乙烯基硅橡胶45-60份、丁苯树脂20-30份、氧化镁18-28份、煅烧陶土8-15份、气相法白炭黑8-12份、碳酸钙5-15份、稳定剂3-7份、乙醇10-15份、硬脂酸钡6-12份、阻燃剂2-5份和复合增效剂4-7份。2.根据权利要求1所述一种矿井用抗弯折电缆外护套材料,其特征在于,按照重量份由以下成分组成:甲基乙烯基硅橡胶55-60份、丁苯树脂26-30份...
【专利技术属性】
技术研发人员:何俊文,唐俊丽,唐青松,
申请(专利权)人:新宇电缆集团股份有限公司,
类型:发明
国别省市:安徽,34