一种新型的超疏水彩色喷墨打印薄膜介质结构制造技术
A new super hydrophobic color inkjet printing film dielectric structure
The utility model relates to a novel super hydrophobic color ink-jet printing film medium structure, which is the main body of a plastic film with a single-layer columnar half opening structure on the surface. The plastic film can achieve color jet ink jet printing without coating treatment, and completely avoids some problems caused by the introduction of ink absorbing coating. At the same time, the plastic substrate itself has super hydrophobic characteristics, making the image printed by this special plastic film also has excellent waterproof and antifouling characteristics.
【技术实现步骤摘要】
一种新型的超疏水彩色喷墨打印薄膜介质结构
本专利涉及一种彩色喷墨打印介质的结构，具体涉及一种具有超疏水特性的彩色喷墨打印介质的结构。
技术介绍
随着彩喷技术的不断革新，彩喷打印机的打印质量不断提高，价格则不断下降。彩喷打印已逐渐成为商务广告、室内装饰和仿真艺术品等的主要选择。相应的，彩喷打印介质也随之迅速发展，品质要求越来越高。为了使普通基材能够适应高质量的彩喷打印输出，通常的做法是在基材的表面涂覆吸墨层，这不仅耗费资源增加成本，且涂层本身的防水性、耐候性、稳定性等往往会成为影响彩喷打印产品长期使用（特别是户外长期使用）的新增因素。
技术实现思路
本技术的目的在于克服现有技术的不足，提供一种具有超疏水特性，不含吸墨涂层即能实现高质量彩喷打印的薄膜介质的结构。本实验新型为实现上述目的，采取了以下技术方案：一种超疏水彩色喷墨打印薄膜介质的结构，其特征在于其主体是一种表面具有单层柱状半开孔结构的塑料薄膜。本技术中的塑料薄膜的材质是水接触角大于90°的疏水性塑料，其厚度为100~200μm。本技术中的塑料薄膜的表面单层半开孔的孔径为1~10μm，孔的深度为5~15μm，孔密度为108~109个/cm3，且孔的顶部与空气联通。本技术相对于现有技术，具有以下优点：本技术所提供的塑料薄膜结构，其表面单层孔的最小尺寸大于喷墨打印时墨滴的尺寸，且由于孔与空气联通，使得墨滴能够有效进入孔的内部并储存在孔内。因此，塑料薄膜表面的单层孔起到了相当于传统彩喷打印介质中吸墨涂层的吸墨作用，使得该塑料薄膜无需涂覆处理即能够实现彩喷喷墨打印，且完全避免了引入吸墨涂层所带来的一些问题。另一方面，由...
【技术保护点】
一种新型的超疏水彩色喷墨打印薄膜介质结构，其特征在于其主体包含一种表面具有单层柱状半开孔结构的塑料薄膜，其表面单层孔的孔径为1~10μm，孔的深度为5~15μm，孔密度为10
【技术特征摘要】
1.一种新型的超疏水彩色喷墨打印薄膜介质结构，其特征在于其主体包含一种表面具有单层柱状半开孔结构的塑料薄膜，其表面单层孔的孔径为1~10μm，孔的深度为5~15μm，孔密度为108~1...