The formaldehyde removal agent provided by the invention is composed of 5% extracts 30% tea polyphenols crude extract, 0.5 distilled wood vinegar extract, 0.05 0.2mol/L water-soluble iron base precursor and distilled water A agent and 2% hydrogen peroxide solution composed of B agent. The formaldehyde removal agent has obvious effect on removing aldehyde, which is natural, convenient and easy to make, and is free from the use of traditional toxic synthetic chemical raw materials. It belongs to the category of green synthesis and green manufacturing, and caters to the needs of low carbon and environmental protection in people's production and life.
【技术实现步骤摘要】
一种甲醛去除剂及其制备方法
本专利技术涉及一种甲醛去除剂及其制备方法,具体涉及由A剂、B剂构成的甲醛去除剂及其制备方法。
技术介绍
众所周知,甲醛是一种强致癌性物质。然而人们在日常生活的方方面面经常受到甲醛残留甚至是超标的影响。目前广泛使用的除醛措施中,主要有依赖于吸附能力的物理方法和利用特定反应的化学手段。这其中物理手段存在着吸附容量饱和后的甲醛残留、释放等问题,传统的化学手段虽然实现了一定程度的低毒化或无毒化,但不可避免仍然使用到毒性的化学原料及产生二次污染。为实现甲醛处理过程的绿色性、环保性,需要进一步探究甲醛去除的方法及措施。
技术实现思路
本专利技术提供了一种甲醛去除剂,其制备过程不再使用有毒性的化学原料及试剂,且可实现高效吸附、转化并去除甲醛的效果。为达到上述的目的,本专利技术采用的技术方案是:一种甲醛去除剂,其由5%-30%茶多酚粗提液、0.5-20%木醋提取液、0.05-0.2mol/L水性铁基前驱物及蒸馏水构成的A剂与2%双氧水液构成的B剂共同组成。本专利技术中所述茶多酚粗提液是由干茶叶放于一定倍数质量的蒸馏水中在90摄氏度温度下蒸煮后,经冷却、真空过滤,收集其滤液制得。本专利技术中所述木醋提取液为木醋原液加以一定倍数体积量的蒸馏水制成;所述木醋原液为粗制木醋液、精制木醋液中的一种。本专利技术中所述水性铁基前驱物为包含但不限于含水氯化铁、含水氯化亚铁、含水硫酸铁、含水硫酸亚铁、含水硝酸铁、含水硝酸亚铁中的一种或几种;所述水性铁基前驱物体积添加量为茶多酚粗提液的10%-60%。本专利技术中所述的甲醛去除剂,其应用时先施用A剂,后再施用B剂。本专 ...
【技术保护点】
一种甲醛去除剂,其特征在于:所述甲醛去除剂由5%‑30%茶多酚粗提液、0.5‑20%木醋提取液、0.05‑0.2mol/L水性铁基前驱物及蒸馏水构成的A剂与2%双氧水液构成的B剂共同组成。
【技术特征摘要】
1.一种甲醛去除剂,其特征在于:所述甲醛去除剂由5%-30%茶多酚粗提液、0.5-20%木醋提取液、0.05-0.2mol/L水性铁基前驱物及蒸馏水构成的A剂与2%双氧水液构成的B剂共同组成。2.如权利要求1所述的甲醛去除剂,其特征在于:所述茶多酚粗提液是由干茶叶放于一定倍数质量的蒸馏水中在90摄氏度温度下蒸煮后,经冷却、真空过滤,收集其滤液制得。3.如权利要求1所述的甲醛去除剂,其特征在于:所述木醋提取液为木醋原液加以一定倍数体积量的蒸馏水制成。4.如权利要求3所述的甲醛去除剂,其特征在于:所述木醋原液为粗制木醋液、精制木醋液中的一种。5.如权利要求1所述的甲醛去除剂,其特征在于:所述水性铁基前驱物为包含但不限于含水氯化铁、含水氯化亚铁、含水硫酸铁、含水硫酸亚铁、含水硝酸铁、含水...