The invention discloses a high temperature resistant soaking formula, including the first bath formula and second bath formula, according to the weight portion as follows: the first bath formula includes the following contents: caprolactam sealing isocyanate 40%:55 - 60, RF resin liquid: 25, 60, soft water: 878 \u2013 1200, and the formula of RF resin solution is soft water 42 \u2013 52, sodium hydroxide 5%:10, 12, resorcinol solid: 13 \u2013 20, formaldehyde 37%:25 \u2013 30. The invention provides a high temperature resistant soaking formula, and is especially suitable for producing high temperature conveyor belt over 200 degrees for conveying material temperature, which has the characteristics of high temperature aging performance of the dipping layer and long service life of the conveyer belt, etc.
【技术实现步骤摘要】
一种耐高温的浸胶配方
本专利技术涉及产业织物的
,尤其涉及一种耐高温的浸胶配方。
技术介绍
聚酯产业用纺织品采用聚酯工业丝作为主要原料,聚酯工业丝以其高强度、高模量、耐高温等优异性能已成为产业用纺织品的主要原材料,机械橡胶制品—橡胶输送带、传动带、橡胶胶管所必须的骨架材料,目前已经基本聚酯化。聚酯材料的熔点在264℃,具有良好的耐热性能,因此聚酯浸胶帆布已经普遍替代早先的棉帆布,各类耐高温输送带的应用领域里显示了其强大的优势。发电厂的煤渣、钢铁厂的烧结矿料和矿渣,以及水泥厂、冶炼厂的高温物料的输送,近年来,随着环保要求提高以及自动化程度和输送量的提高,输送距离的进一步延伸,普遍采用输送带替代车辆运输了,因此在这些场合,耐高温橡胶输送带对骨架材料—浸胶帆布的性能指标提出了更高的要求:如何改善浸胶层在长期高温物料的作用下,浸胶层的橡胶耐老化性能。因此,进一步提高浸胶帆布耐热性能,延长输送带的使用寿命,是目前解决高耐热输送带迫切需要解决的一个问题,从而进一步推动织物增强橡胶输送带的发展。目前高耐热输送带帆布的浸胶,普遍采用二浴法浸胶工艺,其中第一浴,采用己内酰胺封闭异氰酸酯和环氧树脂的水溶液处理帆布,但作为改善聚酯的惰性表面,第二浴采用酚醛树脂和VP胶乳的水溶液浸渍织物,改善与帆布与橡胶之间的粘合力。目前出现耐高温性能不好的主要原因是第一浴异氰酸酯自聚反应后生成的聚氨酯层,在橡胶硫化后,在长时间的高温作用下,和胺类的橡胶促进剂残余胺类物资反应,被分解,从而造成粘合层的破坏失效。因此必须改进该层粘合层的耐高温性能,提高浸胶层的粘合力。
技术实现思路
为了克服上述 ...
【技术保护点】
一种耐高温的浸胶配方,其特征在于:包括第一浴配方和第二浴配方,按照重量份如下:其中,第一浴配方包括以下内容:己内酰胺封闭异氰酸酯40%:55‑60RF树脂液:25‑60软水:878–1200;其中RF树脂液的配方为:软水:42–52氢氧化钠5%:10‑12间苯二酚固体:13–20甲醛37%:25–30。
【技术特征摘要】
1.一种耐高温的浸胶配方,其特征在于:包括第一浴配方和第二浴配方,按照重量份如下:其中,第一浴配方包括以下内容:己内酰胺封闭异氰酸酯40%:55-60RF树脂液:25-60软水:878–1200;其中RF树脂液的配方为:软水:42–52氢氧化钠5%:10-12间苯二酚固体:13–20甲醛37%:25–30。2.根据权利要求...