A rust resistant cell phone shell metal surface treatment agent, which is characterized by the preparation of each component of the following weight: Castor Oil 2, 12, 5, 10, two, 2, 6, 10, three terpenoid, three terpenoid, 1, 6, sodium silicate, sodium silicate, chitosan, and chitosan 3, 15, alumina 5, 17, sodium pyrophosphate 1, 9, deionized water 5, 15. The metal shell surface treatment agent made by the invention can improve the fine degree of the mobile phone, such as the thineness and the cool, and so on. The metal cell shell after the invention has the advantages of good texture and high strength, and has the absolute advantage in the aspects of wear resistance, antioxidation, anticorrosion and rust prevention. The invention has the advantages of low cost, safe use, no pollution to the environment, and good popularization and application.
【技术实现步骤摘要】
一种防锈蚀手机壳金属表面处理剂
本专利技术属于金属表面处理
,具体地说,涉及一种防锈蚀手机壳金属表面处理剂。
技术介绍
金属表面处理剂指对金属表面进行各种处理的化学药剂的总称。金属在加工、处理及使用过程中经常会发生不同程度的氧化、腐蚀等,降低金属材料或金属设备的使用寿命,因此,需要对金属表面进行处理,增加其抗氧化、抗腐蚀的能力,延长使用寿命。涂装是金属表面处理常用的技术,在涂装过程中磷化会产生大量的含磷废水,并且需要在强酸或强碱性条件下进行,对人的身体健康和环境造成极大的危害。随着手机外观精细度的要求越来越高,如纤薄度、酷炫度等,金属手机外壳在手机外观上的使用也越来越多。金属手机外壳具有质感良好、强度高的优点,但是它存在耐磨性能差、抗氧化能力弱、容易锈蚀等问题,故其在市场上就很难占据优势。因此,急需一种对环境无污染,不损害人身体健康,耐磨耐腐,抗氧化能力好的手机壳金属表面处理剂。
技术实现思路
本专利技术针对上述现有技术的不足,提供一种防锈蚀手机壳金属表面处理剂。本专利技术的技术方案是:一种防锈蚀手机壳金属表面处理剂,其特征是,包括以下重量份的各组份制备而成:蓖麻油2-12份、石蜡5-10份、二苯胺2-6份、聚乙烯醇10-25份、三萜皂基1-6份、对苯二甲酸2-8份、枸缘酸钠0.5-3份、金属锌2-10份、壳聚糖3-15份、氧化铝5-17份、焦磷酸钠1-9份、去离子水5-15份。所述聚乙烯醇为15-20份。所述枸缘酸钠为1-1.5份。所述对苯二甲酸4-6份。本专利技术制得的手机金属壳表面处理剂,可提高手机外观精细度如纤薄度、酷炫度等,采用本专利技术后的金 ...
【技术保护点】
一种防锈蚀手机壳金属表面处理剂,其特征是,包括以下重量份的各组份制备而成:蓖麻油2‑12份、石蜡5‑10份、二苯胺2‑6份、聚乙烯醇10‑25份、三萜皂基1‑6份、对苯二甲酸2‑8份、枸缘酸钠0.5‑3份、金属锌2‑10份、壳聚糖3‑15份、氧化铝5‑17份、焦磷酸钠1‑9份、去离子水5‑15份。
【技术特征摘要】
1.一种防锈蚀手机壳金属表面处理剂,其特征是,包括以下重量份的各组份制备而成:蓖麻油2-12份、石蜡5-10份、二苯胺2-6份、聚乙烯醇10-25份、三萜皂基1-6份、对苯二甲酸2-8份、枸缘酸钠0.5-3份、金属锌2-10份、壳聚糖3-15份、氧化铝5-17份、焦磷酸钠1-9份、去离子水...