A quenching method for 45# steel workpiece is characterized by the following steps: placing the workpiece in a heating device, heated to 850, 900, and 1.5 for 3 hours; quenched with a 60 quencher at 80 centigrade and tempering 450 at 550 C; the quench agent consists of the following weight components: potassium chloride 1 5 copies, benzoate Acid sodium 0.5, 1, sodium chloride 0.5, 3, water 10, 20. The quenching method of a kind of 45# steel workpiece put forward by the invention has good quenching effect, and the steel will not appear cracking, and it can overcome the problem of rust after the steel quenching, reduce the waste of resources and save the cost of manufacturing.
【技术实现步骤摘要】
一种45#钢材工件的淬火方法
本专利技术属于材料热处理
，具体是一种45#钢材工件的淬火方法。
技术介绍
45#钢是目前广泛使用的一种优质碳素结构钢，由于45#钢经调质处理后，具有良好的综合机械性能，因此制作某些关键零件(尺寸为Φ5-Φ12)时，设计图纸大都要求选用冷拉45圆钢进行调质(淬火+高温回火)处理。现有的45#钢材的淬火方法一般是加热到820-860℃盐水淬火，540℃回火，这样淬火处理钢材常会出现淬火开裂的情况，导致零件报废，往往需要重新投产，报废率增加，造成资源浪费且增加成本。
技术实现思路
本专利技术的目的在于针对上述问题，提出一种用于45#钢材工件的淬火方法。为了实现上述目的，本专利技术采用以下技术方案来实现。依据本专利技术提出的一种45#钢材工件的淬火方法，包括以下步骤：将工件摆放在加热设备中，加热到850-900℃，保温1.5-3小时；用60-80℃的淬火剂进行淬火，450-550℃回火；所述的淬火剂由以下重量份的物质组成：氯化钾1-5份，苯甲酸钠0.5-1份，氯化钠0.5-3份，水10-20份。为了实现上述目的，本专利技术还采用以下技术措施来进一步实现。进一步的，所述的淬火剂由以下重量份的物质组成：氯化钾1份，苯甲酸钠0.5份，氯化钠0.5份，水10份。进一步的，所述的淬火剂由以下重量份的物质组成：氯化钾5份，苯甲酸钠1份，氯化钠3份，水20份。本专利技术提出的一种45#钢材工件的淬火方法淬火效果好，钢材不会出现开裂现象，且克服钢材淬火后生锈的问题，减少资源浪费，节省制造成本。上述说明仅是本专利技术技术方案的概述，为了能更清楚了解...
【技术保护点】
一种45#钢材工件的淬火方法，其特征在于包括以下步骤：将工件摆放在加热设备中，加热到850‑900℃，保温1.5‑3小时；用60‑80℃的淬火剂进行淬火，450‑550℃回火；所述的淬火剂由以下重量份的物质组成：氯化钾1‑5份，苯甲酸钠0.5‑1份，氯化钠0.5‑3份，水10‑20份。
【技术特征摘要】
1.一种45#钢材工件的淬火方法，其特征在于包括以下步骤：将工件摆放在加热设备中，加热到850-900℃，保温1.5-3小时；用60-80℃的淬火剂进行淬火，450-550℃回火；所述的淬火剂由以下重量份的物质组成：氯化钾1-5份，苯甲酸钠0.5-1份，氯化钠0.5-3份，水10-20份。2.根据...
【专利技术属性】
技术研发人员：贾留宽，王红超，贾若龙，
申请(专利权)人：洛阳神佳窑业有限公司，
类型：发明
国别省市：河南,41