The invention relates to a ceramic - coated frying tea pot, including: an iron fried tea pot and a ceramic coating covered on the inner surface of the fried tea pot; the ceramic coating is made of the following weight ratio material: 3% to 5% glass fibers, 1% to 3% talcum powder, 0.5% to 1% aluminum powder, 0.2% to 0.3% titanium powder, 0.1% to 0.12% oxidation. Magnesium; the allowance is ceramic clay and unavoidable impurities. The ceramic coating frying pot provided by the invention adds ceramic coating to the traditional iron pot. Ceramic coating has high hardness and compactness; it can protect the internal iron pot effectively; at the same time, ceramic or heat bad conductor can slow the temperature raising speed of the saute tea pot, and effectively avoid the lower quality of the tea caused by the high temperature.
【技术实现步骤摘要】
一种陶瓷涂层炒茶锅
本专利技术涉及一种陶瓷涂层炒茶锅，属于炒茶
技术介绍
传统炒茶，使用的均为铁锅。一般家庭用铁锅在使用时都会加入油，从而产生保护层，避免铁锅锈蚀。炒茶锅则不具有油的保护，并且，炒茶过程中，会产生高温高湿，让铁锅更容易锈蚀。
技术实现思路
本专利技术的目的在于：提出一种防锈蚀的陶瓷涂层炒茶锅。为了解决上述技术问题，本专利技术提出的技术方案是：一种陶瓷涂层炒茶锅，包括：铁制的炒茶锅和覆盖在所述炒茶锅内部表面的陶瓷涂层；所述陶瓷涂层由以下重量比材料烧制而成：3%到5%的玻璃纤维、1%到3%的滑石粉、0.5%到1%的铝粉、0.2%到0.3%的钛粉，0.1%到0.12%的氧化镁；余量为陶瓷黏土和不可避免的杂质。本专利技术提供的陶瓷涂层炒茶锅，在传统铁锅内增加陶瓷涂层。陶瓷涂层具有极高的硬度、致密性；可以有效保护内部铁锅；同时，陶瓷还是热的不良导体，可以减缓炒茶锅的温度提升速度，有效避免温度过高导致的茶叶品质降低。具体实施方式实施例本实施例的陶瓷涂层炒茶锅，包括：铁制的炒茶锅和覆盖在炒茶锅内部表面的陶瓷涂层；陶瓷涂层由以下重量比材料烧制而成：3%到5%的玻璃纤维、1%到3%的滑石粉、0.5%到1%的铝粉、0.2%到0.3%的钛粉，0.1%到0.12%的氧化镁；余量为陶瓷黏土和不可避免的杂质。本专利技术不局限于上述实施例的具体技术方案，除上述实施例外，本专利技术还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案，均落在本专利技术要求的保护范围。
【技术保护点】
一种陶瓷涂层炒茶锅，其特征在于，包括：铁制的炒茶锅和覆盖在所述炒茶锅内部表面的陶瓷涂层；所述陶瓷涂层由以下重量比材料烧制而成：3%到5%的玻璃纤维、1%到3%的滑石粉、0.5%到1%的铝粉、0.2%到0.3%的钛粉，0.1%到0.12%的氧化镁；余量为陶瓷黏土和不可避免的杂质。
【技术特征摘要】
1.一种陶瓷涂层炒茶锅，其特征在于，包括：铁制的炒茶锅和覆盖在所述炒茶锅内部表面的陶瓷涂层；所述陶瓷涂层由以下重量比材料烧制而成：3%到5%...