The invention relates to a multilayer folding nonwoven production and relates to the preparation method of non-woven fabrics, it is characterized by the following: the weight ratio of material made of polypropylene, lauryl alcohol polyoxyethylene ether, diatomite, ethyl acrylate, epoxy propane, propylene glycol, butyl vinyl ether, propylene glycol fatty acid ester; the preparation method is: the heating material stirring to 120 to 130 DEG C to melt and then pulled into a folded non-woven fabric, using professional mechanical folding into multi folded non-woven fabric. The invention can multilayer fold without leaving creases, solve the problem of unfolding of non-woven fabrics, and reduce production energy consumption, increase the adhesion of ink, and reduce the loss of ink.
【技术实现步骤摘要】
一种多层折叠无纺布
本专利技术涉及无纺布的生产及制备方法。
技术介绍
随着电商的掘起，无纺布网络零售出现了新高潮，如：无纺布墙纸、摄影用背景纸、农用薄膜、床单等，但是幅宽大的无纺布快递运输成为电商发展鸡肋，很多专业性的无纺布产品（如：墙纸、摄影背景纸等）都需要平整无折痕，可以一般不能折叠，需要用纸筒卷起来，这样就为快递运输造成不便，首先包装成本高，额外增加了纸筒和外包装的成本，第二：快递费高，由于超出快递公司限定的标准长，所以要额外增加快递费用，第三：在快递过程中容易损坏，第四：仓储成本，大量的不同规格的纸筒要占用很大的仓库空间，解决无迹折叠成为无纺布行业电商发展的重要课题。
技术实现思路
本专利技术一种多层折叠无纺布，可以多层折叠不留折痕，解决了无纺布无迹折叠的问题，而且降低生产能耗、增加油墨的附着力，减少油墨的损耗。为实现上述目的，本专利技术采用以下技术方案：聚丙烯91～95份、月桂醇聚氧乙烯醚3～5份、硅藻土6～11份、丙烯酸羟乙酯1～2份、环氧丙烷1.5～2份、丙二醇1.2～2.2份、丁基乙烯基醚2～3份、丙二醇脂肪酸酯0.5～0.8份；制作方法：将上述材料加热搅拌至120℃～130℃溶化后再拉成折叠无纺布，再采用专业机械折叠成多层折叠无纺布。；本专利技术采用多层折叠均不留折痕，解决降低了无纺布的运输、包装和仓储成本，同时降低了聚丙烯的溶点，降低生产能耗、增加油墨的附着力，减少油墨的损耗。具体实施方式一种多层折叠无纺布，本专利技术采用以下技术方案：聚丙烯92份、月桂醇聚氧乙烯醚4份、硅藻土8份、丙烯酸羟乙酯1.5份、环氧丙烷1.8份、丙二醇1.9、丁基...
【技术保护点】
一种多层折叠无纺布，其特征是采用以下材料重量比例制成：聚丙烯91～95份、月桂醇聚氧乙烯醚3～5份、硅藻土6～11份、丙烯酸羟乙酯1～2份、环氧丙烷1.5～2份、丙二醇1.2～2.2份、丁基乙烯基醚2～3份、丙二醇脂肪酸酯0.5～0.8份；制作方法：将上述材料加热搅拌至120℃～130℃溶化后再拉成折叠无纺布，再采用专业机械折叠成多层折叠无纺布。
【技术特征摘要】
1.一种多层折叠无纺布，其特征是采用以下材料重量比例制成：聚丙烯91～95份、月桂醇聚氧乙烯醚3～5份、硅藻土6～11份、丙烯酸羟乙酯1～2份、环氧丙烷1.5～2份、丙二醇1....
【专利技术属性】
技术研发人员：邓宏昌，
申请(专利权)人：广东协宏无纺布科技有限公司，
类型：发明
国别省市：广东,44