The invention discloses a preparation method of a composite flocculant with low cost, which includes the following steps: aluminum sulfate, ferrous chloride, zinc chloride, polyaluminum chloride, ferric sulfate and mixed evenly, adding diatomite, vermiculite powder, water soluble starch and polyacrylamide mixing composite flocculant has low cost. The method is simple, low cost, wide source of raw materials, the flocculant dosage, flocculation and flocculation of excitation effect is good, low cost, and can increase the flocculation ability, so as to enhance the water treatment effect, reduce the two pollution risk, improve water quality, and have good quality stability, shelf life long, have a good ability to adapt to the natural environment, easy to use.
【技术实现步骤摘要】
一种成本低廉的复合絮凝剂制备方法
本专利技术涉及絮凝剂
,尤其涉及一种成本低廉的复合絮凝剂制备方法。
技术介绍
无机混凝剂主要为铝盐、铁盐,研究表明单一的铝盐、铁盐会使得出水存在铝盐、铁盐二次沉积现象;而单一有机高分子混凝剂的性能会受到pH值影响较大,主要原因是有机高分子物质在不同的pH值时,以不同的单体物质存在;因此制备一种絮凝效果好且成本低的絮凝剂是当前主要的研究方向。
技术实现思路
基于
技术介绍
存在的技术问题,本专利技术提出了一种成本低廉的复合絮凝剂制备方法,方法简便,原料来源广泛,成本低廉,所得絮凝剂投料量小,絮凝激发效果好,絮凝处理成本低廉,同时可增加絮凝沉积能力,从而提升了水处理效果,降低了二次污染风险,提高处理后水质,同时具有良好的质量稳定性,保质期长,对自然环境具有良好的适应能力,使用方便。本专利技术提出的一种成本低廉的复合絮凝剂制备方法,包括如下步骤:将硫酸铝、氯化亚铁、氯化锌、聚合氯化铝、聚合硫酸铁混合均匀,再加入硅藻土、蛭石粉、水溶性淀粉、聚丙烯酰胺混合均匀得到成本低廉的复合絮凝剂。优选地,硫酸铝、氯化亚铁、氯化锌、聚合氯化铝的重量比为40-60:30-50:30-40:15-25。优选地,硫酸铝、硅藻土、蛭石粉的重量比为40-60:4-8:4-6。优选地,硫酸铝、水溶性淀粉、聚丙烯酰胺的重量比为40-60:7-13:4-8。本专利技术方法简便,原料来源广泛,成本低廉,所得絮凝剂投料量小,絮凝激发效果好,絮凝处理成本低廉,同时可增加絮凝沉积能力,从而提升了水处理效果,降低了二次污染风险,提高处理后水质,同时具有良好的质量稳定性,保质 ...
【技术保护点】
一种成本低廉的复合絮凝剂制备方法,其特征在于,包括如下步骤:将硫酸铝、氯化亚铁、氯化锌、聚合氯化铝、聚合硫酸铁混合均匀,再加入硅藻土、蛭石粉、水溶性淀粉、聚丙烯酰胺混合均匀得到成本低廉的复合絮凝剂。
【技术特征摘要】
1.一种成本低廉的复合絮凝剂制备方法,其特征在于,包括如下步骤:将硫酸铝、氯化亚铁、氯化锌、聚合氯化铝、聚合硫酸铁混合均匀,再加入硅藻土、蛭石粉、水溶性淀粉、聚丙烯酰胺混合均匀得到成本低廉的复合絮凝剂。2.根据权利要求1所述成本低廉的复合絮凝剂制备方法,其特征在于,硫酸铝、氯化亚铁、氯化锌、聚合氯化铝的重量比为40...
【专利技术属性】
技术研发人员:何明兴,
申请(专利权)人:芜湖上水源环保科技有限公司,
类型:发明
国别省市:安徽,34