The present invention relates to an optical film for advertising, composed of a base layer and a surface layer, wherein the substrate layer is polyethylene film, the adhesive layer comprises the following components in part by weight: 44 E epoxy resin 12 30 copies, 10 copies, 5 butyl acrylate methyl acrylamide 5 9, ISO 10 cyanate ester 18, polyethylene 2 5 copies, 25 copies, 20 rosin ethyl silicate 1 3, propylene glycol ether acetate 1 2, 5 acrylate monomer 9, ethyl acetate 10 15 copies, 10 copies of Phenone two 8. The advertising light film used in the invention has the effect of crystal and bright, bright and colorful, and no color change for a long time. It has soft touch and colorful surface color. It is a kind of safety and environmental protection material.
【技术实现步骤摘要】
一种广告用光膜
本专利技术涉及光膜领域,尤其是涉及一种广告用光膜。
技术介绍
在纸制品上裱一层透明的塑料薄膜,就是覆膜。覆膜分为“光膜”和“哑膜”。具体来说,像产品说明书印刷中的封面、纸盒的外表面这些容易磨损的部位,如果需要保护膜,就在印刷之后、折叠和裁切之前给它裱一层,这层膜必须很透明,有很好的韧性,质地均匀,没有砂眼气泡,表面很平整,它通常是聚丙烯材料做成的,它还预涂了热塑性高分子粘合剂以便和纸张结合,印刷厂用热压滚筒把它牢牢地贴在纸上。这样一来,纸的表面有了更好的光泽,质地更厚实,而且印在上面的颜色受到了保护。当今的铜版纸封面一般都要覆膜,高档的纸盒和手提袋、产品说明书和企业宣传册的封面、挂历、服装上的商标等也要覆膜。光膜最透明,对墨色几乎没有影响,在精装书封面、硬纸盒等平整的表面上,光亮如镜的效果非常好的。
技术实现思路
本专利技术的目的是提供一种广告用光膜,用于解决现有技术存在的问题。为了实现上述专利技术目的,本专利技术的技术方案具体如下:一种广告用光膜,由基材层和背胶层组成,所述基材层为聚乙烯薄膜,所述背胶层由下述组分按重量份组成:E-44环氧树脂12-30份、丙烯酸丁酯5-10份、甲基丙烯酰胺5-9份、异氰酸酯10-18份、聚乙烯2-5份、松香20-25份、正硅酸乙酯1-3份、丙二醇甲醚醋酸酯1-2份、丙烯酸酯单体5-9份、醋酸乙酯10-15份、二苯甲酮8-10份。进一步地,所述背胶层由下述组分按重量份组成:E-44环氧树脂18份、丙烯酸丁酯9份、甲基丙烯酰胺8份、异氰酸酯15份、聚乙烯3份、松香24份、正硅酸乙酯2份、丙二醇甲醚醋酸酯2份、丙烯 ...
【技术保护点】
一种广告用光膜,其特征在于:由基材层和背胶层组成,所述基材层为聚乙烯薄膜,所述背胶层由下述组分按重量份组成:E‑44环氧树脂12‑30份、丙烯酸丁酯5‑10份、甲基丙烯酰胺5‑9份、异氰酸酯10‑18份、聚乙烯2‑5份、松香20‑25份、正硅酸乙酯1‑3份、丙二醇甲醚醋酸酯1‑2份、丙烯酸酯单体5‑9份、醋酸乙酯10‑15份、二苯甲酮8‑10份。
【技术特征摘要】
1.一种广告用光膜,其特征在于:由基材层和背胶层组成,所述基材层为聚乙烯薄膜,所述背胶层由下述组分按重量份组成:E-44环氧树脂12-30份、丙烯酸丁酯5-10份、甲基丙烯酰胺5-9份、异氰酸酯10-18份、聚乙烯2-5份、松香20-25份、正硅酸乙酯1-3份、丙二醇甲醚醋酸酯1-2份、丙烯酸酯单体5-9份...
【专利技术属性】
技术研发人员:孙子昂,
申请(专利权)人:成都雅途视界文化传播有限公司,
类型:发明
国别省市:四川,51