The invention relates to an inorganic modified co polymer plugging agent; according to the weight percentage composition is: 1-10% acrylamide and 0.1-2% N, N- two methyl acrylamide monomer 1-4%, citric acid, 2-3%, 1-3% bentonite 10-30% silicate, calcium carbonate, 0.01-1% ammonium persulfate and balance water; the first fully dissolved acrylamide, N, N- two methyl acrylamide monomer, followed by adding citric acid, bentonite, silicate, calcium carbonate and stirring evenly; the plugging agent is injected into the well, after the main part of the organic gelling plugging agent with strong toughness and inorganic part can obviously improve the plugging agent the strength and temperature resistance, tested its gelling after consistency can reach more than 70bc and cement, the constant temperature of 120 DEG C for more than 3 months do not break, no hydrolysis, acidification of reservoir damage is small, suitable for high temperature wells in the open Gas channeling during mining to block construction.
【技术实现步骤摘要】
本专利技术涉及用于石油开采的调堵剂及其配制方法,是一种无机改性共聚物调堵剂。
技术介绍
目前油田上使用的调堵剂主要分无机类和有机类两大种,无机类调堵剂的主要缺点是:对油藏的伤害大、施工风险高、不易解堵。有机类堵剂的主要缺点是:耐温性不高,主要用于90℃以下油藏的调堵作业,成胶后的强度偏低,受油藏温度、配液水质的矿化度影响较大易水解破胶。
技术实现思路
本专利技术的目的是提供一种无机改性共聚物调堵剂,具有耐温性能高、封堵强度大、对油藏伤害小、施工风险低、易解堵的优点。本专利技术的技术方案之一是这样来实现的:一种无机改性共聚物调堵剂,其按重量百分比组成为:1-10%的丙烯酰胺、0.1-2%的N,N-二甲基丙烯酰胺单体、1-4%的柠檬酸、2-3%的坂土、1-8%的硅酸盐、10-30%的碳酸钙、0.01-1%的过硫酸铵和余量的水。本专利技术的技术方案之二是这样来实现的:一种无机改性共聚合物调堵剂的配制方法,其特征在于按下述步骤进行:无机改性共聚物调堵剂配制:首先将所需要量的丙烯酰胺、N,N-二甲基丙烯酰胺单体依次加入到总水量中,充分搅拌溶解,其次在搅拌下分别加入所需要量的过硫酸铵、柠檬酸、坂土、硅酸盐、碳酸钙。本专利技术的特点:所得到的无机改性共聚物调堵剂配制方法简单且效率高,具有耐温性能高、封堵强度大、对油藏伤害小、施工风险低、易解堵的优点。该无机改性共聚物调堵剂适用于高温开 ...
【技术保护点】
一种无机改性共聚合物调堵剂,其特征在于:按重量百分比组成为:1‑10%的丙烯酰胺、0.1‑2%的N,N‑二甲基丙烯酰胺单体、1‑4%的柠檬酸、2‑3%的坂土、1‑8%的硅酸盐、10‑30%的碳酸钙、0.01‑1%的过硫酸铵和余量的水。
【技术特征摘要】
1.一种无机改性共聚合物调堵剂,其特征在于:按重量百分比组
成为:1-10%的丙烯酰胺、0.1-2%的N,N-二甲基丙烯酰胺单体、1-4%
的柠檬酸、2-3%的坂土、1-8%的硅酸盐、10-30%的碳酸钙、0.01-1%
的过硫酸铵和余量的水。