The invention discloses a building decoration paste consisting of acrylic emulsion, vinegar, cellulose, silica sol, calcium carbonate, calcium carbonate powder, putty powder, components according to weight ratio of acrylic acid emulsion: vinegar: cellulose: silica sol: calcium carbonate: Shuangfei powder =1-25%:1-10%:1-3%:1-8%:1-18%: 1-25%; the invention has high light resistance, weatherability, alkali resistance, water resistance, wet scrubbing, with features of delicate, bright color, good texture, good adhesion with cement materials, abundant raw materials, cheap Tesco; production, simple construction technology, decorative effect is good, rich in color, wide application range.
【技术实现步骤摘要】
本专利技术涉及建筑装饰技术，特别涉及的是一种用于建筑内外墙面装饰的建筑装饰膏。
技术介绍
目前，随着建筑业的快速发展，建筑涂料技术也相对增多。现有的涂料趋于水溶性和无溶性两大类。这两大类的特点是无毒、无公害，价格低，易于施工，有较好的市场，但这类涂料观感粗糙，不耐擦洗，制造成本较高。
技术实现思路
本专利技术的目的是为了提供一种无毒、无放射性元素、粘结力强，耐光、耐候性良好，耐擦洗、表面光滑细腻，色泽多样，使用热能极少，价格低廉的建筑装饰膏。为实现上述技术目的，本专利技术采取的技术方案是：一种建筑装饰膏，其特征在于：所述装饰膏由丙烯酸醋乳液、纤维素、硅溶胶、碳酸钙、双飞粉、腻子粉组成，各组分按重量比为：丙烯酸醋乳液：纤维素：硅溶胶：碳酸钙：双飞粉=1-25%：1-10%：1-3%：1-8%：1-18%：1-25%；由于采取上述技术方案，本专利技术具有高耐光性、耐候性、不泛黄性，还具有优良的耐碱、耐水、耐湿擦洗性，还具有外观细腻、色泽艳丽、质感好、与水泥材料附着力好等特点，加入了适量的硅溶胶，其涂膜不易产生静电，不易吸附灰尘，耐污染性好，涂膜对基层渗透能力强，附着性好；加入碳酸钙，降低了成本，提高工效；原材料来源丰富，价廉易购；生产、施工工艺简单，装饰面效果好，色泽丰富，适用范围广。具体实施方式：下面结合实施例对本专利技术做进一步说明：一种建筑装饰膏，其由丙烯酸醋乳液、纤维素、硅溶胶、碳酸钙、双飞粉、腻子粉组成，各组分按重量比为：丙烯酸醋乳液：纤维素：硅溶胶：碳酸钙：双飞粉=1-2...
【技术保护点】
一种建筑装饰膏，其特征在于：所述装饰膏由丙烯酸醋乳液、纤维素、硅溶胶、碳酸钙、双飞粉、腻子粉组成，各组分按重量比为：丙烯酸醋乳液：纤维素：硅溶胶：碳酸钙：双飞粉=1‑25%：1‑10%：1‑3%：1‑8%：1‑18%：1‑25%。
【技术特征摘要】
1.一种建筑装饰膏，其特征在于：所述装饰膏由丙烯酸醋乳液、纤维素、硅溶胶、碳酸钙、双飞粉、腻子粉组成，各组分按重量比为：...