Chrome free tanning wet white leather production process, the technological process is as follows: gray skin graft after washing, deliming - acid - - - decolorization tanning drum, stationary, synthetic tanning agent (zirconium, aluminum, Titanium Tanning) is a kind of auxiliary tanning agent, its performance is decentralized, acceleration, or osmotic adjustment and combination of other tanning agents, and accelerate the absorption of fats, not only reduces the environmental pollution, eliminate damage of six chromium on the human body, and the leather quality compared with chrome tanned leather has improved significantly.
【技术实现步骤摘要】
本专利技术涉及白湿皮制作工艺,特别涉及无铬鞣白湿皮制作工艺。
技术介绍
众所周知制造高质量的轻革在所有无机鞣剂中,铬鞣剂是首屈一指的,但人们对六价铬的剧毒却深恶痛疾,为铬盐资源的短缺忧心忡忡。铝鞣的革收缩温度可达80度左右,革色洁白,粒面紧密细致,革身轻巧,延伸性也较好;缺点不耐水洗,成革扁薄,丰满性差。锆鞣的革收缩温度可达95度左右,锆鞣剂填充效果好,革身丰满坚实,颜色洁白,粒面紧密细致,耐磨性好,锆鞣革性质稳定,耐久贮;缺点易吸水,易变型,鞣革稍显板硬,撕裂强度稍差。钛鞣的革收缩温度97度左右,钛鞣吸收率太别高,达95%以上,可消除污染,保护环境。钛鞣的革颜色洁白,柔软丰满,弹性好,革身紧密,耐光、耐洗、耐贮存、耐磨性能较好。合成鞣剂是一种辅助性鞣剂,其性能是分散、加速、或调节其它鞣剂的渗透和结合,并加速油脂的吸收。
技术实现思路
本专利技术的目的是解决以上问题,求得高质量的轻革而研发了除铬盐以外的其它无机鞣剂(锆、铝、钛结合鞣)代替铬鞣剂制造出白湿皮。本专利技术是通过以下制作工艺来实现的:无铬鞣白湿皮制作工艺,其工艺流程为:灰皮片皮后水洗——脱灰——脱色——浸酸——鞣制——出鼓、静止,具体步骤如下:第一步、灰皮片皮后水洗,液比:2,温度常温;第二步、脱灰,液比:1温度30℃,1.5%DEL;0.01%PX-1,0.3%NS,PH:8.0左右排水;第三步、脱色,液比:2,温度常温,3%NaCL,0.3%KmnO4,1.6%焦亚硫酸钠,0.3%草酸,0. ...
【技术保护点】
无铬鞣白湿皮制作工艺,其特征在于:其工艺流程为:灰皮片皮后水洗——脱灰——脱色——浸酸——鞣制——出鼓、静止。
【技术特征摘要】
1.无铬鞣白湿皮制作工艺,其特征在于:其工艺流程为:灰皮片皮后水洗——脱灰——脱色——浸酸——鞣制——出鼓、静止。
2.根据权利要求1所述的无铬鞣白湿皮制作工艺,其特征在于:所述灰皮片皮后水洗的液比为:2,温度常温。
3.根据权利要求1所述的无铬鞣白湿皮制作工艺,其特征在于:所述的脱灰,其液比:1,温度30℃,1.5%DEL,0.01%PX-1,0.3%NS,PH:8.0排水。
4.根据权利要求1所述的无铬鞣白湿皮制作工艺,其特征在于:所述的脱色,液比:...