The invention relates to a high-strength low resistivity graphite composite material preparation method, which is characterized in that the raw material components weight percentages are as follows: (1) according to the weight percentage: particle size of natural graphite powder 1-70 m 30 ~ 50%, the particle size of 1-30 m B4C 1 to Si 8%, powder particle size 1-70 m from 2 to 8%, the particle size of 1-30 m ZrO2 2 ~ 25%, 20 ~ 40% binder of the raw materials are evenly mixed. The invention has the advantages of natural graphite itself, low stability, low resistivity, volatile component and thermal expansion coefficient, and has the advantages of simple process and short production cycle.
【技术实现步骤摘要】
本专利技术主要涉及石墨复合材料,尤其涉及一种一种高强低电阻率石墨复合材料制备方法。
技术介绍
石墨材料属于新能源材料中的负极材料,石墨具有质软、有滑腻感,是一种非金属矿物质,有耐高温、耐氧化、抗腐蚀、抗热震、强度大、韧性好、直润滑强度高、导热导电性能强等特有的物理化学性能。因而被广泛用于化工、航天、核能等领域。特别在各种核聚变装置中采用。天然石墨与其它石油焦、沥青焦相比,具有较高热稳定性、较低电阻率、挥发份和热膨胀系数。
技术实现思路
本专利技术的目的是提供一种高强低电阻率石墨复合材料制备方法。本专利技术由以下技术方案来实现:一种高强低电阻率石墨复合材料制备方法,其特征在于原料组份重量百分比如下:(1)按重量百分比:粒径为1-70um的天然石墨粉30~50%、粒径为1-30um的B4C1~8%、粒径为1-70um的Si粉2~8%、粒径为1-30um的ZrO22~25%、粘结剂20~40%;将上述原料均匀混合;(2)在2500~2700℃、压力为18~38MP下热压成型,恒温时间5~60min,制取该高强低电阻率石墨复合材料。本专利技术优点:具有天然石墨本身稳定性、较低电阻率、挥发份和热膨胀系数优良特征:工艺操作简单,生产周期短。具体实施例:本专利技术的实施例如下:实施例1一种高强低电阻率石墨复合材料制备方法,其特征在于原料组份重量百分比如下:(1)按重量百分比:粒径为5 ...
【技术保护点】
一种高强低电阻率石墨复合材料制备方法,其特征在于原料组份重量百分比如下:(1)按重量百分比:粒径为1‑70um的天然石墨粉30~50%、粒径为1‑30um的B4C1~8%、粒径为1‑70um的Si粉2~8%、粒径为1‑30um的ZrO22~25%、粘结剂20~40%;将上述原料均匀混合。(2)在2500~2700℃、压力为18~38MP下热压成型,恒温时间5~60min,制取该高强低电阻率石墨复合材料。
【技术特征摘要】
1.一种高强低电阻率石墨复合材料制备方法,其特征在于原料组份重量百分比如下:
(1)按重量百分比:粒径为1-70um的天然石墨粉30~50%、粒径为1-30um的B4C1~
8%、粒径为1-70um的Si粉2~8%、...