The invention discloses a method for improving Aluminum Alloy casting hardness formula and structural strength, which comprises the following components by weight percent of silicon, accounted for 16 ~ 19%, 1.5 ~ 2% iron, copper accounted for 0.8 to 1.2%, accounting for 0.5 to 1% lead, cadmium accounted for 0.01 ~ 0.02%, 1 ~ 2% of titanium, tungsten trioxide accounted for 6 three ~ 9%, 0.5 ~ 2% of molybdenum oxide, the other is aluminum. The components of the invention are evenly stirred, then poured into a graphite furnace or an electric furnace, and then heated and melted into a die casting die, and an aluminum alloy die casting is obtained by die casting. The present invention further improves its surface hardness and structural strength under the premise of maintaining a low cost advantage.
【技术实现步骤摘要】
一种提高硬度及结构强度的铝合金压铸配方
本专利技术涉及铝合金压铸配方
,尤其是涉及一种提高硬度及结构强度的铝合金压铸配方。
技术介绍
现有技术中,铝合金具有密度小、硬度高、结构强度高等优良的物理性能,同时具有重量轻、密度小、成本低的竞争优势,铝合金广泛用于各个领域,然而,技术是不断向前发展的,如何在保持低成本的价格优势的前提下进一步提高其性能,如提高其表面硬度和结构强度,这是需要不断改进的。
技术实现思路
针对现有技术存在的不足,本专利技术的目的是提供一种提高硬度及结构强度的铝合金压铸配方,它在保持低成本的价格优势的前提下进一步提高其表面硬度和结构强度。为了实现上述目的,本专利技术所采用的技术方案是。一种提高硬度及结构强度的铝合金压铸配方,包括以下重量百分比的组分,硅占16~19%,铁占1.5~2%,铜占0.8~1.2%,铅占0.5~1%,镉占0.01~0.02%,钛占1~2%,三氧化钨占6~9%,三氧化钼0.5~2%,其余为铝。进一步的技术方案中,所述铝合金压铸配方包括以下重量百分比的组分,包括以下重量百分比的组分,硅占17~18%,铁占1.7~1.8%,铜占0.8~0.9%,铅占0.6~0.7%,镉占0.01~0.02%,钛占1~2%,三氧化钨占6~7%,三氧化钼1.1~1.3%,其余为铝。本专利技术和现有技术相比所具有的优点是:本专利技术在保持低成本的价格优势的前提下进一步提高其表面硬度和结构强度。具体实施方式以下所述仅为本专利技术的较佳实施例,并不因此而限定本专利技术的保护范围。实施例一一种提高硬度及结构强度的铝合金压铸配方,包括以下重量百分比的 ...
【技术保护点】
一种提高硬度及结构强度的铝合金压铸配方,其特征在于:包括以下重量百分比的组分,硅占16~19%,铁占1.5~2%,铜占0.8~1.2%,铅占0.5~1%,镉占0.01~0.02%,钛占1~2%,三氧化钨占6~9%,三氧化钼0.5~2%,其余为铝。
【技术特征摘要】
1.一种提高硬度及结构强度的铝合金压铸配方,其特征在于:包括以下重量百分比的组分,硅占16~19%,铁占1.5~2%,铜占0.8~1.2%,铅占0.5~1%,镉占0.01~0.02%,钛占1~2%,三氧化钨占6~9%,三氧化钼0.5~2%,其余为铝。2.根据权利要求1所述的一种提高硬度及结构强度的铝合金压铸配方,其特征在于:所述铝合金压铸配方包括以下重量百分比的...
【专利技术属性】
技术研发人员:王其领,
申请(专利权)人:东莞市淦宏信息科技有限公司,
类型:发明
国别省市:广东,44