The invention discloses a compound antifreeze, consists of the following parts by weight of the ingredients: two DEG 10~20, 0.5~1 zinc tungstate, sodium nitrite 10~15, ethylene glycol 10~20, silicate stabilizer 1~3, triethanolamine 5~10, sodium alginate 2~3; brassinolide 0.1~0.5; vinyl acetate 0.3~0.5, deionized water 10~15. The present invention is not frozen, at -45 DEG C for lost foam time less than 3 seconds, the positively charged metal ions of carboxylate polymers and poly sulfonated styrene sulfonic acid with ethylene glycol and water solution have adsorption effect, form protective membrane, protect the metal from corrosion, and the invention does not contain nitrite along with phosphate, has the advantages of environmental protection advantages, based on the anti freezing effect and give full play to the good corrosion inhibition effect.
【技术实现步骤摘要】
复合防冻液
本专利技术属于防冻液
，尤其是一种由高聚物形成金属保护膜的新型高效复合防冻液配方。
技术介绍
市场上防冻液中的缓蚀剂很多含有磷酸盐或亚硝酸盐，这种缓蚀剂在使用后会对环境产生污染。市场上防冻液中的缓蚀剂主要分为：阳极型缓蚀剂和阴极型缓蚀剂，由于汽车是由不同成分的金属构件构成的，而不同成分的金属构件构成需用不同的缓蚀剂，亚硝酸钠对钢铁、铸铁的缓蚀效果好，但对焊料产生孔蚀，这些单品种缓蚀剂虽成本较低，但难以满足防冻液诸多方面的性能要求。
技术实现思路
针对现有技术存在的不足，本专利技术所要解决的技术问题是，提供一种对多种金属有效、能在金属表面形成保护膜，保护金属不被腐蚀的新型高效复合防冻液配方。为解决上述技术问题，本专利技术所采取的技术方案是：复合防冻液，其特征在于，由以下重量份的成份组成：二甘醇10~20份，钨酸锌0.5~1份，亚硝酸钠10~15份，乙二醇10~20份，硅酸盐稳定剂1~3份，三乙醇胺5~10份，海藻酸钠2～3份；芸苔素0.1～0.5份；醋酸乙烯酯0.3～0.5份，去离子水10～15份。本专利技术新型高效复合防冻液配方的优点是：本专利技术在-45℃不结冰、泡沫消失时间小于3秒钟，高聚物的羧酸根及聚磺化苯乙烯的磺酸根与乙二醇、水溶液中带正电荷的金属离子产生吸附作用，形成保护膜，保护金属不被腐蚀，且本专利技术不含亚硝酸沿，不含磷酸盐，具有优越的环保性，在防冻效果的基础上充分发挥了良好的缓蚀效果。具体实施方式下面结合具体实施例对本专利技术做进一步详细说明；实施例1：复合防冻液，其特征在于，由以下重量份的成份组成：二甘醇10~20份，钨酸锌...
【技术保护点】
复合防冻液，其特征在于，由以下重量份的成份组成：二甘醇10~20 份，钨酸锌0.5~1 份，亚硝酸钠10~15 份，乙二醇10~20份，硅酸盐稳定剂1~3 份，三乙醇胺5~10 份，海藻酸钠 2～3份；芸苔素 0.1 ～0.5 份；醋酸乙烯酯 0.3～0.5份，去离子水10～15份。
【技术特征摘要】
1.复合防冻液，其特征在于，由以下重量份的成份组成：二甘醇10~20份，钨酸锌0.5~1份，亚硝酸钠10~15份，乙二醇10~20份，...