The invention provides a high wet starch adhesive: including the weight ratio of the raw materials are as follows: potato starch 100, sorbitol 5, ammonium sulfate 1, carboxymethyl cellulose 15, tert-butyl perbenzoate 2 copies, 40 copies of acrylic latex, 12 copies, 1 copies of borax Na2PO3F, 3 copies, 5 copies of polyacrylamide, vinyl acetate 10, 1,2 benzo isothiazolin ketone 3 2.5 copies, 3 copies of the melamine formaldehyde resin, deionized water 1600, stearic acid 5. The present invention has antibacterial, toughening effect, with moisture absorption ability, control coating moisture, prevent dry, enhance the strength of coating layer, application layer of dense coating after gel smooth, non-toxic, dry and wet strength qualified, good toughness.
【技术实现步骤摘要】
一种高湿强淀粉胶黏剂
本专利技术涉及胶黏剂，尤其涉及一种高湿强淀粉胶黏剂。
技术介绍
现有建筑胶黏剂湿强度不够，并且在粘结疏水物质时粘结力明显不够。
技术实现思路
本专利技术的目的提供一种高湿强淀粉胶黏剂，解决上述现有技术问题中的一个或者多个。根据本专利技术的一个方面，提供一种高湿强淀粉胶黏剂：包括重量份数比如下的原料：马铃薯淀粉100份，山梨糖醇5份，过硫酸铵1份，羧甲基纤维素15份，过氧化苯甲酸叔丁酯2份，丁苯乳液40份，丙烯酸酯12份，硼砂1份，单氟磷酸钠3份，聚丙烯酰胺5份，醋酸乙烯10份，1,2-苯并异噻唑啉-3-酮2.5份，三聚氰胺甲醛树脂3份，去离子水1600份，硬脂酸5份。本专利技术提供的高湿强淀粉胶黏剂，具有抗菌防腐、增韧补强效果，具备一定的吸湿能力，控制涂料层的水分，防止干裂，增进涂料层强度，施胶后的涂料层致密光滑，环保无毒，干、湿强度合格，韧性良好。具体实施方式根据本专利技术的一个方面，提供一种高湿强淀粉胶黏剂：包括重量份数比如下的原料：马铃薯淀粉100份，山梨糖醇5份，过硫酸铵1份，羧甲基纤维素15份，过氧化苯甲酸叔丁酯2份，丁苯乳液40份，丙烯酸酯12份，硼砂1份，单氟磷酸钠3份，聚丙烯酰胺5份，醋酸乙烯10份，1,2-苯并异噻唑啉-3-酮2.5份，三聚氰胺甲醛树脂3份，去离子水1600份，硬脂酸5份。本专利技术提供的高湿强淀粉胶黏剂，具有抗菌防腐、增韧补强效果，具备一定的吸湿能力，控制涂料层的水分，防止干裂，增进涂料层强度，施胶后的涂料层致密光滑，环保无毒，干、湿强度合格，韧性良好。以上所述仅是本专利技术的一种实施方式，应当指出，对...
【技术保护点】
一种高湿强淀粉胶黏剂，其特征在于：包括重量份数比如下的原料：马铃薯淀粉100份，山梨糖醇5份，过硫酸铵1份，羧甲基纤维素15份，过氧化苯甲酸叔丁酯2份，丁苯乳液40份，丙烯酸酯12份，硼砂1份，单氟磷酸钠3份，聚丙烯酰胺5份，醋酸乙烯10份，1,2‑苯并异噻唑啉‑3‑酮2.5份，三聚氰胺甲醛树脂3份，去离子水1600份，硬脂酸5份。
【技术特征摘要】
1.一种高湿强淀粉胶黏剂，其特征在于：包括重量份数比如下的原料：马铃薯淀粉100份，山梨糖醇5份，过硫酸铵1份，羧甲基纤维素15份，过氧化苯甲酸叔丁酯2份，丁苯乳液40...