The present invention discloses plasticized wood plastic materials, consists of the following parts by weight of the composition of polyvinyl chloride resin 10 ~ 20; wood powder 20 ~ 50 and 5 ~ 12; zinc borate; impact agent 10 ~ 15 and 2 ~ 5; epoxy butyl oleate; sodium molybdate 4 ~ 5 and 2 ~ 4; liquid paraffin; sorbitol 0.4 Magnesium Oxide 3 ~ ~ 0.6; 5; 20 ~ 30 ligneous plant fiber; paraffin 3 ~ 5. The invention adopts renewable, environmental protection, new wood plastic materials and without any harm to the human body to replace the traditional plastic injection molding material mainly, the cheap material (such as, can be trees, leaves, sawdust, industrial sheet and other scrap), single can be greatly reduced the use of plastic and change injection molding material, product stability and made strong, no shrinkage, but also can be used repeatedly.
【技术实现步骤摘要】
增塑木质注塑材料
本专利技术涉及增塑木质注塑材料。
技术介绍
目前市场上的很多注塑产品主要是以苯乙烯、聚碳酸酯及聚苯乙烯等注塑材料形成,这些材料一方面含有诸多有害化学成分,会对人体健康造成伤害,另一方面成本较高,不能回收利用,且废弃后难以降解,会造成严重的环境污染。
技术实现思路
针对现有技术存在的不足,本专利技术所要解决的技术问题是,提供一种具有环保、对人体无任何伤害和可循环再生等特点,且成本低廉,从而克服了现有技术中不足的增塑木质注塑材料。为解决上述技术问题,本专利技术所采取的技术方案是:一种增塑木质注塑材料,其特征在于,由以下重量份的成分组成:聚氯乙烯树脂10~20;木粉20~50;硼酸锌5~12;抗冲击剂10~15;环氧油酸丁酯2~5;钼酸钠4~5;液体石蜡2~4;山梨醇0.4~0.6;氧化镁3~5;木化植物纤维20~30;石蜡3~5。本专利技术增塑木质注塑材料的优点是:本专利技术采用可循环再生、环保,且对人体无任何伤害的新型木质注塑材料替代了传统以塑料为主的注塑材料,其原料廉价易得(如,可以是树木,树叶,木屑,工业板材的边角料等),可大幅减少塑料的使用和改变注塑材质的单一性,同时制成的产品稳定性强,无收缩变形,还可反复回收使用。具体实施方式下面结合具体实施例对本专利技术做进一步详细说明;一种增塑木质注塑材料,其特征在于,由以下重量份的成分组成:聚氯乙烯树脂10~20;木粉20~50;硼酸锌5~12;抗冲击剂10~15;环氧油酸丁酯2~5;钼酸钠4~5;液体石蜡2~4;山梨醇0.4~0.6;氧化镁3~5;木化植物纤维20~30;石蜡3~5。当然,上述说 ...
【技术保护点】
增塑木质注塑材料,其特征在于,由以下重量份的成分组成:聚氯乙烯树脂 10~20;木粉 20~50;硼酸锌 5~12;抗冲击剂 10~15;环氧油酸丁酯 2~5;钼酸钠 4~5;液体石蜡 2~4;山梨醇 0.4~0.6;氧化镁 3~5;木化植物纤维 20~30;石蜡 3~5 。
【技术特征摘要】
1.增塑木质注塑材料,其特征在于,由以下重量份的成分组成:聚氯乙烯树脂10~20;木粉20~50;硼酸锌5~12;抗冲击剂10~...