The invention discloses a composite insulation cloth manufacturing method, which comprises the following steps: providing a bottom protective film, protection film at the bottom of the release paper, in accordance with the requirements of cutting off the paper will be divided into shape; conductive cloth tape cut to release paper, conductive cloth tape attaching surface a layer of weakly viscous protective film punching, conductive cloth tape required shape, eliminate waste; insulation tape in weakly viscous protective film, positioning punching a desired shape; peeling bottom protective film, the fixture for the product neatly folded. The invention realizes the easy punching, cutting and cutting of the compound insulating cloth, and reduces the manufacturing cycle of the product.
【技术实现步骤摘要】
复合绝缘布制造方法
本专利技术属于薄膜或薄片状的黏合剂
，尤其涉及一种复合绝缘布制造方法。
技术介绍
随着电子行业的逐渐发展，复合布类产品的应用越来越广泛，传统的切膜机效率不高，存在切断粘连不易切开的问题，以及排废困难，复合布的良品率不高，浪费原材料，生产成本增加。传统的复合布的制造方法为：冲切导电布，将导电布按图纸要求冲切形状，冲切定位孔，用于二次冲型时套位，导电布自带离型纸结合力大，造成排废困难，定位孔容易变形；贴合绝缘布，贴合保护膜，最后定位冲切导电布的离型纸面，排废包装。此工艺需要多台及其设备多次冲型贴合才能完成，存在导电布孔位变形，切断困难等问题。
技术实现思路
本专利技术的目的是为了解决上述技术问题，而提供一种复合绝缘布的制造方法，从而实现复合绝缘布的易冲切切断，减少产品制造周期。为了达到上述目的，本专利技术技术方案如下：复合绝缘布制造方法，包括以下步骤：S1，提供一种底部保护膜，底部保护膜贴合离型纸，按照要求冲切离型纸形状；S2，将分切好的导电布胶带贴合于离型纸上，导电布胶带表面贴合一层弱粘性保护膜，冲切导电布胶带所需形状，排除废料；S3，在弱粘性保护膜上贴合绝缘布胶带，定位冲切所需形状；S4，剥除底部保护膜，用治具将产品整齐收叠。具体的，所述底部保护膜为PET保护膜。具体的，所述底部保护膜的粘性大于18N。具体的，所述离型纸的离型力为15-18g。与现有技术相比，本专利技术复合绝缘布的制造方法的有益效果主要体现在：通过在导电布胶带上贴合弱粘性保护膜有利于导电布胶带的冲切，排废简单；通过底部保护膜使得整个工艺处于稳定状态，便于生产作业；在弱...
【技术保护点】
复合绝缘布制造方法，其特征在于，包括以下步骤：S1，提供一种底部保护膜，底部保护膜贴合离型纸，按照要求冲切离型纸形状；S2，将分切好的导电布胶带贴合于离型纸上，导电布胶带表面贴合一层弱粘性保护膜，冲切导电布胶带所需形状，排除废料；S3，在弱粘性保护膜上贴合绝缘布胶带，定位冲切所需形状；S4，剥除底部保护膜，用治具将产品整齐收叠。
【技术特征摘要】
1.复合绝缘布制造方法，其特征在于，包括以下步骤：S1，提供一种底部保护膜，底部保护膜贴合离型纸，按照要求冲切离型纸形状；S2，将分切好的导电布胶带贴合于离型纸上，导电布胶带表面贴合一层弱粘性保护膜，冲切导电布胶带所需形状，排除废料；S3，在弱粘性保护膜上贴合绝缘布胶带，定位冲切所需形状；S4，剥...