The invention relates to a two-component aqueous epoxy resin coating, which belongs to the field of coating and chemical engineering. The waterborne epoxy resin coatings including A and B components, A components include: water-based epoxy resin wt%, zinc 60~70 30~50 colloidal wt%, graphene microchip 0.5~3 wt%, pigments and fillers and additives 10~20 wt%; B group was divided into two p-phenylenediamine as primary amine compounds the water epoxy curing agent; control of waterborne epoxy resin emulsion and waterborne epoxy curing agent mass ratio is 4~8:1. Waterborne epoxy resin coatings prepared by the invention has the advantages of simple operation, using water as solvent without VOCs emission, the film surface smoothness, good flexibility (less than 1), strong adhesion (less than 1), high gloss, excellent acid and alkali resistance, water resistance, salt fog resistance.
【技术实现步骤摘要】
一种水性环氧树脂涂料
本专利技术涉及一种水性环氧树脂涂料,属涂料化工领域。
技术介绍
腐蚀问题一直是影响国民经济发展的重要因素。我国每年因腐蚀造成的经济损失约占GDP的3%~5%,2014年全年腐蚀损失超过2.1万亿元。防腐领域,特别是重防腐领域,其涂料体系一般要求配套使用,包括底漆、中涂和面漆。底漆是涂层基础,是涂层最重要的部分。底漆含有较多的颜填料,必须对基体具有良好的润湿性和附着力,同时还要有较强的屏蔽性和耐酸碱性。由于环氧树脂与基体间的附着力好,固化剂种类多,固化后体积收缩仅有2%,固化后能形成三维网状结构,具有较好的耐水性、耐酸碱性、耐油性,所以环氧富锌涂料是防腐领域中应用最广泛涂料之一。溶剂型环氧涂料含有大量挥发性有机物(VolatileOrganicCompounds,VOCs),VOCs是造成光化学烟雾的主要原因,它会引发慢性呼吸道疾病、损伤中枢神经、刺激黏膜、致癌致畸等,所以控制VOCs的排放量势在必行。因此,国家出台了一系列政策法规来限制VOCs的排放,水性环氧富锌涂料是目前涂料发展的一大趋势。但是环氧树脂不溶于水,制备水性环氧富锌涂料需要将环氧树脂水性化,目前常用方法有:机械法、化学改性法、外加乳化剂法等。现有技术水性化后只能够形成一种乳液,稳定性、亲水性以及环氧树脂在乳液中存在的尺寸大小并不能完全满足要求。
技术实现思路
本专利技术所要解决的技术问题是克服现有水性环氧富锌涂料用乳液制备的不足,提供一种水性环氧树脂胶体制备水性环氧树脂涂料的方法。本专利技术采用的技术方案是:一种水性环氧树脂涂料,包括A组分和B组分,其特征在于,所述水性环氧 ...
【技术保护点】
一种水性环氧树脂涂料,由组分A和组分B水性环氧固化剂组成,其特征在于, 所述水性环氧树脂涂料A组分包括:水性环氧树脂胶体30~50 wt%、锌粉30~70 wt%、石墨烯微片0.5~3 wt%、颜填料10~20 wt%。
【技术特征摘要】
1.一种水性环氧树脂涂料,由组分A和组分B水性环氧固化剂组成,其特征在于,所述水性环氧树脂涂料A组分包括:水性环氧树脂胶体30~50wt%、锌粉30~70wt%、石墨烯微片0.5~3wt%、颜填料10~20wt%。2.根据权利要求1所述的水性环氧树脂涂料,其特征是:所述水性环氧树脂是以水性环...
【专利技术属性】
技术研发人员:刘海萍,张松,毕四富,左银成,王春雨,曹立新,
申请(专利权)人:哈尔滨工业大学威海,
类型:发明
国别省市:山东,37