The invention discloses a flame retardant conductive rubber formula reinforced a nano materials, made from the following raw materials in parts by weight: 30 silicone rubber 60, nano sulfobetaine micelles 5 stearic acid 10, 3 6 copies, 10 copies of 5 inorganic flame retardant chloroprene rubber, 20 30 copies, 4 promoters 12, copper 5 8 copies, 20 copies of 10 black. The size of the conductive powder in accordance with the size of the large and small diameter is extremely close, the purpose is to achieve the highest filling rate, so as to achieve the best conductivity. In use, it will not crack because of ozone. Even when exposed to the flame, it will not burn. It will not corrode either in the air or in the ground. The utility model can withstand the impact of the instantaneous high current, and has the function of multi-point continuous earthing.
【技术实现步骤摘要】
一种纳米材料增强的阻燃导电橡胶配方
本专利技术涉及橡胶配方
,具体涉及一种纳米材料增强的阻燃导电橡胶配方。
技术介绍
导电按键、导电橡胶辊筒等都采用了导电橡胶,主要是作为电流导电、防静电等租用。近几十年来,随着各种电器的普及,电子计算机、通讯卫星、高压输电网和一些医用设备等的广泛应用,由此带来的电磁辐射污染也越来越严重。为此,必须进行电磁屏蔽,因此,出现了各种电磁屏蔽材料产品,导电橡胶就是其中的一种,目前市场上的导电橡胶多是普通非阻燃等级,尤其是以镍包石墨为填料的导电橡胶,高阻燃等级更是不多。所以在一些对阻燃要求高的场合,普通级别的导电橡胶,其应用受到了一定的限制。
技术实现思路
针对现有技术的不足,本专利技术所要解决的技术问题是,提供一种高强度、阻燃、导电性能优异、同事具有阻燃特性的纳米材料增强的阻燃导电橡胶配方。为解决上述技术问题,本专利技术所采取的技术方案是:一种导电橡胶配方,由以下重量份数的原料制成:硅橡胶30-60份,纳米磺酸甜菜碱胶束5-10,硬脂酸3-6份,无机阻燃剂5-10份,氯丁橡胶20-30份,促进剂4-12份,铜粉5-8份,炭黑10-20份。上述的导电橡胶配方,由以下重量份数的原料制成:硅橡胶40份,纳米磺酸甜菜碱胶束8,硬脂酸5份,无机阻燃剂7份,氯丁橡胶25份,促进剂8份,铜粉6份,炭黑15份。本专利技术纳米材料增强的阻燃导电橡胶配方的优点是:将导电粉体按照大、小粒径进行粒径极配的目的是为了达到最高填充率,从而达到最佳的导电率。且在使用过程中不会因为臭氧而开裂,即使暴露在火焰中也不会延燃,无论在空气中和地下都不会被腐蚀。可以承受 ...
【技术保护点】
一种纳米材料增强的阻燃导电橡胶配方,其特征在于,由以下重量份数的原料制成:硅橡胶30‑60份,纳米磺酸甜菜碱胶束5‑10,硬脂酸3‑6份,无机阻燃剂5‑10份,氯丁橡胶20‑30份,促进剂4‑12份,铜粉5‑8份,炭黑10‑20份。
【技术特征摘要】
1.一种纳米材料增强的阻燃导电橡胶配方,其特征在于,由以下重量份数的原料制成:硅橡胶30-60份,纳米磺酸甜菜碱胶束5-10,硬脂酸3-6份,无机阻燃剂5-10份,氯丁橡胶20-30份,促进剂4-12份,铜粉5-8份,炭...